Dissolution and separation of non-metallic powder from printed circuit boards by using chloride solvent
Autor: | Wenyi Yuan, Kaiyou Huang, Huabo Duan, Jingwei Wang, Junying Xie, Xiaodan Li, Xiaoyan Wang, Chenglong Zhang, Yang Yuhan, Wang Lincai, John C. Crittenden, Jianfeng Bai |
---|---|
Rok vydání: | 2021 |
Předmět: |
Reaction mechanism
Materials science 020209 energy Ethyl acetate Thermosetting polymer 02 engineering and technology 010501 environmental sciences 01 natural sciences Electronic Waste Catalysis chemistry.chemical_compound Chlorides Spectroscopy Fourier Transform Infrared 0202 electrical engineering electronic engineering information engineering Recycling Waste Management and Disposal Dissolution 0105 earth and related environmental sciences Aqueous solution Epoxy Solvent Solubility chemistry Chemical engineering visual_art Solvents visual_art.visual_art_medium Powders |
Zdroj: | Waste Management. 123:60-68 |
ISSN: | 0956-053X |
Popis: | Non-metallic components (NMC) in waste printed circuit boards (WPCBs) are made of the thermosetting epoxy resin and glass fiber, which has been a research concern in the waste recycling area. The recycling of thermosetting epoxy resin is a serious challenge due to their permanent cross-linked structure. An efficient approach to chemical recycling of epoxy resin for resource reutilization was developed in this research. ZnCl2/CH3COOH aqueous solution was selected as catalysts system to decompose epoxy resin under a mild reaction condition. The influence of reaction parameters such as reaction temperature, time, liquid-solid ratio and ZnCl2 amount on the decomposition efficiency of epoxy resin and reaction mechanism were investigated. The physical and chemical properties of NMC, reaction solvent and decomposed products were analyzed using scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR) and Gas chromatography–mass spectrometry (GC–MS). Results showed that up to 81.85% of epoxy resin could be dissolved by using a temperature of 190 °C during 8 h with a mixture of acetic acid (15 wt%): ZnCl2 (5 g) 20 mL/g. Incompletely coordinated zinc ions enables the cleavage of C N, C Br and C O bonds in the thermosetting brominated epoxy resin, which was mainly converted to phenol, 2-Bromophenol and 2, 4-Dibromophenol with high resource value. And the functional groups of ethyl acetate and acetic acid maintained chemical structure before and after reaction. This research provided a practical approach to the dissolution and reutilization of NMC in WPCBs. |
Databáze: | OpenAIRE |
Externí odkaz: |