Peculiarity of seed-layer synthesis and morphometric characteristics of ZnO nanorods
| Autor: | Oleksandr Bogdan, Anatolii Orlov, Veronika Ulianova, Genadzi Pashkevich |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2014 |
| Předmět: |
Materials science
Applied Mathematics Mechanical Engineering зародковий шар золь-гель гідротермальний метод нанострижні ZnO Energy Engineering and Power Technology Industrial and Manufacturing Engineering Computer Science Applications UDC 539.23 Chemical engineering Control and Systems Engineering Management of Technology and Innovation seed-layer ZnO nanorods sol-gel hydrothermal method tilting Nanorod Electrical and Electronic Engineering зародышевый слой гидротермальный метод наностержни ZnO Layer (electronics) Sol-gel |
| Zdroj: | Eastern-European Journal of Enterprise Technologies; Том 6, № 12(66) (2013): Physical and technological problems of radio engineering devices, telecommunication, nano-and microelectronics; 72-75 Восточно-Европейский журнал передовых технологий; Том 6, № 12(66) (2013): Физико-технологические проблемы радиотехнических устройств, средств телекоммуникаций, нано-и микроэлектроники; 72-75 Східно-Європейський журнал передових технологій; Том 6, № 12(66) (2013): Фізико-технологічні проблеми радіотехнічних пристроїв, засобів телекомунікацій, нано-і мікроелектроніки; 72-75 |
| ISSN: | 1729-3774 1729-4061 |
| Popis: | Представлено оригінальні результати синтезу нанострижнів ZnO за допомогою низькотемпературних методів на підкладках ніобату літію. Вперше продемонстровано «орієнтовані канали», які виникають після відпалу зародкового шару при температурі 400°С і свідчать про початок процесу кристалізації. Проаналізовано вплив властивостей зародкового шару ZnO, сформованого золь-гель методом, на морфометричні характеристики синтезованих гідротермальним методом нанострижнів. The obtained new results of ZnO hexagonal nanorods synthesis by hydrothermal method on the lithium niobate substrate with synthesized seed-layer from sol-gel were presented. Optical microscopy, scanning electron microscopy and X-ray diffractometry were used to examine the morphometric and structural characteristics of the formed structures. The “oriented channels” for deposited by sol-gel method ZnO seed-layers was detected after annealing for the first time. It could be evidence of crystalline structure formation of the layer and wasn’t caused by the process on the interface between the layer and the substrate. It was established that the roughness of the ZnO seed-layer had significant influence on ZnO nanorods structure and caused its tilting. The diameter of single seeds had defined the diameter of nanorods obtained by hydrothermal method and was about 50 nm, the length of nanorods was about 0,5 µm. Average aspect ratio was equal to 9.3. The ZnO rod structures were regularly situated all over the substrate surface and had single-crystal structure. It is expected that vertically oriented ZnO structures can be obtained on smooth seed-layer, formed at adjusted process parameters such as sol-gel concentration and annealing temperature. The synthesized nanostructures could be applied as single functional material of nanoscale devices, such as sensing element of surface acoustic wave sensors and energy storage cells for energy harvesting due to having unique properties. Представлены оригинальные результаты синтеза наностержней ZnO с помощью низкотемпературных методов на подложках ниобата лития. Впервые продемонстрированы «ориентированные каналы», которые возникают после отжига зародышевого слоя при температуре 400°С и свидетельствуют о начале процесса кристаллизации. Проанализировано влияние свойств зародышевого слоя ZnO, сформированного золь-гель методом, на морфометрические характеристики синтезированных гидротермальным методом наностержней. |