Influence of Indentation on the Fatigue Strength of Carbonitrided Plain Steel
| Autor: | Junwen Zhao, Zhenyu Zhu, Guangze Dai, Gao Jiewei, Lei Xu, Li Hengkui |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
Materials science
Article Subject Scanning electron microscope Significant difference General Engineering Fatigue limit body regions Indentation lcsh:TA401-492 Fracture (geology) lcsh:Materials of engineering and construction. Mechanics of materials General Materials Science Composite material Layer (electronics) |
| Zdroj: | Advances in Materials Science and Engineering, Vol 2015 (2015) |
| ISSN: | 1687-8442 1687-8434 |
| DOI: | 10.1155/2015/492693 |
| Popis: | To study the influence of indentation on the fatigue strength of untreated and carbonitrided specimens of S38C steel, the fatigue limit of specimens with and without indentations was tested. Fracture surfaces were observed using scanning electron microscopy (SEM). The results show that the fatigue strength of the untreated specimen decreases with increasing dimension of indentation, without significant difference compared to the predicted results. Compared to the fatigue limit of the untreated specimen, those of the carbonitrided specimen and the carbonitrided specimen whose compound layer was polished were improved by 12% and 40%, respectively. The fatigue strength of the carbonitrided specimen decreased sharply with increasing indentation size because of the presence of microcracks in the compound layer. When the compound layer was removed, the fatigue limit was observed to be less sensitive to indentation than that of the carbonitrided specimen. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|