Effect of Titanium on Homogenizing Process and Microstructure of Alloy 2618
| Autor: | Jianhua Wang, Ya Liu, Xuping Su, Tingting Liu, Peng Haoping |
|---|---|
| Rok vydání: | 2014 |
| Předmět: |
Technology
Materials science Chemical technology microstructure Alloy Metallurgy homogenization Chemicals: Manufacture use etc chemistry.chemical_element TP200-248 TP1-1185 engineering.material Condensed Matter Physics Microstructure Homogenization (chemistry) 2618-ti alloy chemistry Mechanics of Materials engineering grain refinement General Materials Science Physical and Theoretical Chemistry Titanium |
| Zdroj: | High Temperature Materials and Processes, Vol 33, Iss 3, Pp 261-267 (2014) |
| ISSN: | 2191-0324 0334-6455 |
| DOI: | 10.1515/htmp-2013-0066 |
| Popis: | The effect of titanium on the homogenizing process of alloy 2618 and the microstructure of the Ti-containing alloy before and after homogenization has been investigated using optical microscope (OM), scanning electron microscope (SEM), energy dispersive X-ray (EDX), differential thermal analysis (DTA). The results show that the addition of 1.5 mass% Ti to alloy 2618 could refine its grain size remarkably. A large amount of rod-shape Al3Ti particles with the size range of 2–12 μm distribute evenly and dispersively in the alloy. It is θ (Al2Cu) phase instead of S' (Al2CuMg) obtained in eutectic structures due to the non-equilibrium solidification in casting of 2618-Ti alloy, which is the same as alloy 2618. The optimal homogenization temperature (773 K) for Ti-containing alloy 2618 (2618-Ti alloy) is the same as that of alloy 2618. Combining the results of kinetic analysis and experiments, the optimized homogenizing time for Ti-containing alloy 2618 at 773 K is only 12 h, which is shorter than that for alloy 2618. The shortening of the optimized homogenizing time results mainly from the decrease of the grain size of 2618-Ti alloy. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|