Study of the influence of titanium and niobium particle size on the Ti35Nb alloy production with controlled porosity
| Autor: | Francis Faria Goulart, Alexandre Antunes Ribeiro, Débora Vieira Way, Lais de Souza Alves, Carlos Angelo Nunes, Lucas Moreira Ferreira, Roseli Marins Balestra |
|---|---|
| Rok vydání: | 2022 |
| Předmět: | |
| Zdroj: | Matéria (Rio de Janeiro) v.27 n.4 2022 Matéria (Rio de Janeiro. Online) instacron:RLAM Matéria (Rio de Janeiro), Volume: 27, Issue: 4, Article number: e20220072, Published: 14 OCT 2022 |
| ISSN: | 1517-7076 |
| DOI: | 10.1590/1517-7076-rmat-2022-0072 |
| Popis: | The present work is a continuation of the research carried out in a previous work, with the aim of improving the production of Ti35Nb alloy by reducing the particle size of Ti (from 50–149 Μm to < 53 Μm) and Nb (from 31–500 Μm to < 62 Μm) powders. Micro (MI) and Macroporous (MA) Ti35Nb alloy samples were processed by powder metallurgy. Ammonium bicarbonate (AB) was utilized as pore former additive for processing MA samples. The powders were mixed, uniaxially pressed and then sintered at 1300 ºC for 2 hours under argon atmosphere. The samples were characterized by SEM/EDS, XRD, profilometry, and Vickers hardness test. The porosity levels were determined by geometric method, Archimedes’ principle and quantitative metallographic analysis. The results showed that the processing parameters used in this work successfully produced porous Ti35Nb alloys with completely stabilized β-Ti phase, indicating an enhancement in the methodology when compared with those reported in previous work. Smaller particle sizes influenced positively on the chemical-physical properties of MI and MA samples, since they demonstrated an improvement in the their characteristics, such as: more homogeneous microstructure; better particle consolidation; homogeneous elemental distribution with no relevant chemical contamination; porosity values in accordance with literature; presence of low amounts of titanium oxides on the surfaces which can improve the biocompatibility features; suitable surface roughness parameters for bone implant applications and favouring adhesion of bioceramic coatings; more uniform microhardness values for both samples which make the material with a further predictable mechanical behavior. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|