Clayey soil stabilization using alkali-activated cementitious materials
| Autor: | Jhonathan F. Rivera, R. Mejía de Gutiérrez, Armando Orobio, Nuno Cristelo |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2020 |
| Předmět: |
Soil stabilization
Materials science 0211 other engineering and technologies 020101 civil engineering clayey soil Fly ash 02 engineering and technology Suelo arcilloso engineering.material Alkali-activated cement 0201 civil engineering law.invention Clayey soil Flexural strength law Blast furnace slag 021105 building & construction lcsh:TA401-492 General Materials Science Composite material Materials of engineering and construction. Mechanics of materials Lime soil stabilization Building and Construction Portland cement blast furnace slag Escorias granuladas de horno alto Compressive strength fly ash Cenizas volantes Mechanics of Materials Ground granulated blast-furnace slag engineering TA401-492 lcsh:Materials of engineering and construction. Mechanics of materials Estabilización de suelos Cementitious Cemento activado alcalinamente alkali-activated cement |
| Zdroj: | Materiales de Construccion, Vol 70, Iss 337, Pp e211-e211 (2020) Materiales de Construcción; Vol. 70 No. 337 (2020); e211 Materiales de Construcción; Vol. 70 Núm. 337 (2020); e211 Materiales de Construcción Consejo Superior de Investigaciones Científicas (CSIC) |
| ISSN: | 1988-3226 0465-2746 |
| DOI: | 10.3989/mc.2020.v70.i337 |
| Popis: | In this study, a clayey soil classified as A-7-5 according ASTM D3282, was stabilized using alkali-activated cementitious materials (AAC) added to the soil dry in percentages of 20 and 30%. Fly ash (F1, F2) with high unburned carbon content (up to 38.76%), hydrated lime (L) and granulated blast furnace slag were used. Unconfined compressive strength and flexural strength at 28 days of curing and the durability after 12 wetting-drying cycles were evaluated. The results were compared with a soil-cement reference mixture. The soil treated with AAC-F1L showed a volume expansion of 0.51% and volume contraction of -0.57% compared with the 0.59% expansion and -0.68% contraction of the soil-cement reference mixture. Additionally, the mass loss after the wetting and drying cycles is only 3.74% which is slightly lower than the mass loss of the soil stabilized with ordinary Portland cement (OPC) (3.86%) and well below the value specified in Colombian regulations (7%). En este estudio, un suelo arcilloso clasificado como A-7-5 según ASTM D3282, se estabilizó utilizando materiales activados alcalinamente (AAC) en porcentajes de 20 y 30%. Se utilizaron cenizas volantes (F1, F2) con alto contenido de inquemados (hasta 38,76%), cal hidratada (L) y escoria granulada de alto horno. Se evaluó la resistencia a la compresión confinada y la resistencia a la flexión a 28 días de curado y la durabilidad después de 12 ciclos de humectación-secado. Los resultados se compararon con una mezcla de referencia suelo-cemento. El suelo tratado con AAC-F1L mostró una expansión y contracción volumétrica del 0,51% y -0,57% respectivamente, en comparación con el 0,59% y -0,68% de la mezcla de referencia suelo-cemento. Además, la pérdida de masa después de los ciclos de humectación y secado es sólo 3.74%, valor ligeramente inferior a la del suelo estabilizado con cemento Portland (3.86%) y muy inferior al valor especificado en la normativa colombiana (7%). |