Failure resistance of drilling rig casing pipes with an axial crack
| Autor: | Y. G. Matvienko, Miodrag Arsić, Nenad Gubeljak, Marko Rakin, Aleksandar Sedmak, Bojan Medjo, Živče Šarkoćević |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
Materials science
Drilling rig business.industry education Finite element analysis General Engineering Internal pressure 02 engineering and technology Structural engineering Bending 021001 nanoscience & nanotechnology Pipe-ring specimen Micromechanical modelling Finite element method 020303 mechanical engineering & transports 0203 mechanical engineering Fracture (geology) General Materials Science Composite material Cracked pipe 0210 nano-technology business Displacement (fluid) Casing Plane stress |
| Zdroj: | Engineering Failure Analysis |
| ISSN: | 1350-6307 |
| Popis: | Working conditions of casing pipes in drilling rigs can significantly influence the initiation and development of damage in the material, and therefore also the safe service of the entire system. In this work, an integrity assessment of a pipe with initial defect (machined surface crack) is presented. The position of this defect is on the external surface; unlike transport pipes, where internal surface is often endangered due to the contact with the fluid, casing pipes are also often exposed to damages at the external surface. A pipe segment exposed to internal pressure is examined experimentally and numerically, using the finite element method. Experimental setup included tracking of crack mouth opening displacement (CMOD) values, as well as J integral. Criteria for pipe failure are determined on the finite element (FE) models of the pipe; fracture initiation and plastic collapse are considered as failure mechanisms. Several 3D models with different crack sizes are evaluated. 2D plane strain models are also examined, to determine the applicability limits of this simplified approach. Integrity assessment criteria for the analysed geometries are discussed. Assessment of fracture resistance of the pipeline material is also considered in this work. Besides the standard SENB specimens, Ring specimens cut from the pipe are tested, and the results are compared. Both specimen geometries are modelled using local approach to fracture, by application of the micromechanical Complete Gurson model (CGM), developed by Z.L. Zhang. It is shown that the Ring specimens have similar fracture conditions under bending load as SENB specimens. Since they are much simpler to fabricate from the pipe than standard specimens, it is concluded that they can be used for assessment of fracture of the pipes with axial cracks. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect