Dentin bond strength and nanoleakage of the adhesive interface after intracoronal bleaching
| Autor: | Marcelo Giannini, Vanessa Cavalli, Patricia N R Pereira, Maicon Sebold, Mirela Sanae Shinohara |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Histology
genetic structures 0206 medical engineering Carbamide Peroxide 02 engineering and technology Bleaching Agents 03 medical and health sciences chemistry.chemical_compound 0302 clinical medicine Microscopy Electron Transmission stomatognathic system Adhesives Tensile Strength Borates Tooth Bleaching Dentin medicine Animals Urea Hydrogen peroxide Instrumentation Bond strength Dental Bonding Hydrogen Peroxide 030206 dentistry 020601 biomedical engineering Peroxides stomatognathic diseases Medical Laboratory Technology medicine.anatomical_structure chemistry Dentin-Bonding Agents Cattle sense organs Adhesive Dental Pulp Cavity Anatomy Sodium perborate Carbamide peroxide Nuclear chemistry |
| Zdroj: | Microscopy Research and Technique. 81:428-436 |
| ISSN: | 1059-910X |
| Popis: | This study evaluated dentin bond strength (BS) and nanoleakage of non- and pre-etched dentin immediately (T0 ,), 7 days (T7 ), and 14 days (T14 ) after bleaching. Bovine incisors (150) were selected and half of them submitted to intrapulpal dentin etching (e). Non- and pre-etched dentin were subjected to the following (n = 15): no bleaching/control (C); 35% carbamide peroxide (CP); 35% hydrogen peroxide (35% HP); 25% hydrogen peroxide (25% HP); and sodium perborate (SP). Bleaching agents were applied to the pulp chamber four times within a 72-h interval. Afterwards, pulp chamber dentin was prepared for the BS test at different evaluation times (n = 5): T0 , T7 , and T14 . Composite blocks were built on pulp chamber and sectioned in slices. Slices were reduced to an hour-glass shape with a cross-sectional area of 0.8 mm2 and submitted to microtensile BS test. Two additional specimens for each group were prepared for nanoleakage evaluation by transmission electron microscopy (TEM). Results were analyzed by ANOVA (two-way) and Dunnett's test (p < .05). BS decreased immediately after intracoronal bleaching for both sound and pre-etched dentin (p < .05). At T14 , the BS of non-etched bleached dentin increased for all groups, whereas the pre-etched SPe group presented BS similar to the Ce. Nanoleakage within the hybrid layer was perceptible immediately after bleaching, although a decrease in nanoleakage was observed for all groups at T14 . Adhesive restorations should be performed 7-14 days after bleaching, according to the bleaching agent used. Intracoronal bleaching should be performed preferably with sodium perborate if previous dentin etching is applied. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Plný text