Effect of gamma-irradiation on (PEO/PVP)/Au nanocomposite: Materials for electrochemical and optical applications
| Autor: | A.M. Abdelghany, M.A. Morsi, E.M. Abdelrazek, S.I. Badr |
|---|---|
| Rok vydání: | 2016 |
| Předmět: |
010302 applied physics
Thermogravimetric analysis Materials science Nanocomposite Mechanical Engineering technology industry and agriculture Nanoparticle Nanotechnology macromolecular substances 02 engineering and technology 021001 nanoscience & nanotechnology 01 natural sciences Nanomaterials Crystallinity Mechanics of Materials Colloidal gold 0103 physical sciences lcsh:TA401-492 lcsh:Materials of engineering and construction. Mechanics of materials General Materials Science Thermal stability Irradiation 0210 nano-technology Nuclear chemistry |
| Zdroj: | Materials & Design, Vol 97, Iss, Pp 532-543 (2016) |
| ISSN: | 0264-1275 |
| Popis: | Gold nanoparticles (Au NPs) have been successfully biosynthesized by Chenopodium murale (C. murale) leaf extract. Au NPs were incorporated within polyethylene oxide (PEO)/polyvinyl pyrrolidone (PVP) blend by casting method. Prepared samples were characterized before and after subjecting to successive gamma-irradiation doses (1, 2, 3, 4, 5 Mrad). XRD confirmed the semicrystalline nature of blend which was largely decreased after embedding Au NPs and subsequently through high irradiation doses. Before irradiation, FT-IR spectra revealed presence of main vibrational bands due to both PEO and PVP. After irradiation, FT-IR spectra indicated the existence of structural rearrangements in the polymeric matrix due to irradiation process. UV/vis spectra indicated presence of n–π* transition results from single-bond in the backbone of blend and showed a visible band at 531 nm attributed to the surface plasmon resonance of Au NPs that is largely affected by irradiation dose. The values of optical parameters were enhanced due to embedding Au NPs and varied according to the irradiation dose. TEM images showed that particle size range was reduced from 1 to 34 nm for nanocomposite to 4–22 nm after exposure to γ-radiations of 5 Mrad. TGA analysis showed an improvement for the thermal stability of nanocomposite sample after gamma-rays treatment. Keywords: Gamma-irradiation, Nanocomposite, Structural properties, UV/vis, TEM, Thermal stability |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect