Retention Strength of PMMA/UDMA-Based Crowns Bonded to Dentin: Impact of Different Coupling Agents for Pretreatment
| Autor: | Christine Keul, Simona Teuss, Marlis Eichberger, Bogna Stawarczyk, Malgorzata Roos |
|---|---|
| Přispěvatelé: | University of Zurich, Stawarczyk, Bogna |
| Jazyk: | angličtina |
| Rok vydání: | 2015 |
| Předmět: |
Molar
Materials science medicine.medical_treatment 610 Medicine & health cementation lcsh:Technology Article Crown (dentistry) UDMA CAD/CAM polymer PMMA retention strength Dentin medicine Margin Bond Coupling (piping) General Materials Science Composite material Variolink II lcsh:Microscopy lcsh:QC120-168.85 lcsh:QH201-278.5 lcsh:T 10060 Epidemiology Biostatistics and Prevention Institute (EBPI) 2500 General Materials Science medicine.anatomical_structure Distilled water lcsh:TA1-2040 lcsh:Descriptive and experimental mechanics lcsh:Electrical engineering. Electronics. Nuclear engineering lcsh:Engineering (General). Civil engineering (General) lcsh:TK1-9971 |
| Zdroj: | Materials, Vol 8, Iss 11, Pp 7486-7497 (2015) Materials; Volume 8; Issue 11; Pages: 7486-7497 Materials Volume 8 Issue 11 Pages 7486-7497 |
| ISSN: | 1996-1944 |
| Popis: | Computer aided design/computer aided manufacturing (CAD/CAM) polymers for long-term dental restorations benefit from enhanced mechanical properties. However, the quantification of their bonding properties on teeth is lacking. Therefore, the aim of this study was to determine the retention strength (RS) of differently pretreated new developed polymethylmethacrylate/ urethanedimethacrylate-based CAD/CAM polymer bonded on dentin. In summary, 120 human caries-free molars were prepared, and polymeric crowns were milled and pretreated (n = 20): visio.link (VL), Scotchbond Universal (SU), Monobond Plus/Heliobond (MH), Margin Bond (MB), Margin Bond mixed with acetone (1:1) (MBA) or not pretreated (CG). Half of the specimens were cemented using Variolink II and the other half with RelyX Ultimate. Specimens were stored for 24 h in distilled water and thermal cycled (5000 ×, 5 °C/55 °C). The retention load was measured and failure types were defined. RS was calculated and analyzed using both two- and one-way ANOVA with a post-hoc Scheffé-test, unpaired t-test, Kaplan–Meier with Breslow–Gehan test and chi-squared test (p < 0.05). Crowns bonded using RelyX Ultimate showed higher RS than those bonded using Variolink II. The pretreatment showed no impact on the RS. However, survival analysis within Variolink II found an impact of pretreatment. The median RS for MH was the lowest and statistically different from MB, MBA and CG. For Variolink II MH had the poorest survival as the estimated cumulative failure function of the debonded crown increased very quickly with increasing TBS. Within the RelyX Ultimate groups, no significant differences were determined. The newly developed CAD/CAM polymer showed the highest bonding properties after cementation using RelyX Ultimate. |