Self-etch bonding agent beneath sealant: Bond strength for laser-irradiated enamel
Autor: | Jackelline de Lemes Giuntini, Maria Cristina Borsatto, Rodrigo Galo, Jaciara Miranda Gomes-Silva, Carolina Paes Torres, Marta Maria Martins Giamatei Contente |
---|---|
Rok vydání: | 2013 |
Předmět: |
Molar
Materials science Enamel paint Bond strength business.industry Sealant Dentistry shear bond strength stomatognathic system Distilled water pit and fissure sealant visual_art visual_art.visual_art_medium Original Article Adhesive system Adhesive Composite material business Er:YAG laser General Dentistry Acrylic resin |
Zdroj: | European Journal of Dentistry |
ISSN: | 1305-7464 1305-7456 |
DOI: | 10.4103/1305-7456.115412 |
Popis: | Objectives: This study evaluated the in vitro shear bond strength (SBS) of a resin-based pit-and-fissure sealant (Fluroshield [F], Dentsply/Caulk) associated with either an etch-and-rinse (Adper Single Bond 2 [SB], 3M/ESPE) or a two-step self-etch adhesive system (Adper SE Plus [SE], 3M/ESPE) on Er: YAG laser-irradiated enamel. Materials and Methods: Seventeen sound third molar crowns were embedded in acrylic resin, and the mesial-distal enamel surfaces were flattened. The enamel sites were irradiated with a 2.94-μm wavelength Er: YAG laser (120 mJ, 4 Hz, noncontact mode/17 mm, 20 s). The specimens were randomly assigned to three groups according to the bonding technique: I - 37% phosphoric acid etching + SB + F; II - SE + F and III - F applied to acid-etched enamel, without an intermediate layer of bonding agent. In all of the groups, a 3-mm diameter enamel-bonding site was demarcated and the sealant cylinders were bonded. After 24 hours in distilled water, the shear bond strength was tested at a crosshead speed of 0.5 mm/minute. The data were analyzed by one-way ANOVA and Tukey′s test. The debonded specimens were examined with a stereomicroscope to assess the failure modes. Results: The mean SBS values in MPa were I = 6.39 (±1.44); II = 9.50 (±2.79); and III = 5.26 (±1.82). No statistically significant differences were observed between groups I and III; SE/F presented a significantly higher SBS than that of the other groups (P = 0.001). With regard to the failure mode, groups I (65%) and II (75%) presented adhesive failures, while group III showed 50% adhesive failure. Cohesive failure did not occur. Conclusion: The application of the two-step self-etch bonding agent (Adper SE Plus) beneath the resin pit-and-fissure sealant placement resulted in a significantly higher bond strength for the Er:YAG laser-irradiated enamel. |
Databáze: | OpenAIRE |
Externí odkaz: |