Reinforcement of Dental Methacrylate with Glass Fiber after Heated Silane Application
| Autor: | Isabella Negro Favarão, Amanda Vessoni Barbosa Kasuya, Rodrigo Borges Fonseca, Hugo Lemes Carlo, Letícia Nunes de Almeida, Marcella Silva de Paula, Gustavo Adolfo Martins Mendes |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2014 |
| Předmět: |
Fabrication
Materials science Hot Temperature Article Subject General Immunology and Microbiology Glass fiber lcsh:R Dental Cements lcsh:Medicine General Medicine Methacrylate Silane General Biochemistry Genetics and Molecular Biology chemistry.chemical_compound Compressive strength chemistry Flexural strength Dental cement Materials Testing Methacrylates Bisphenol A-Glycidyl Methacrylate Fiber Glass Composite material Research Article |
| Zdroj: | BioMed Research International, Vol 2014 (2014) BioMed Research International |
| ISSN: | 2314-6141 2314-6133 |
| Popis: | This study evaluated the influence of silane heat treatment and glass fiber fabrication type, industrially treated (I) or pure (P), on flexural and compressive strength of methacrylate resin bars (BISGMA/TEGDMA, 50/50%). Six groups(n=10)were created: I-sil: I/silanated; P-sil: P-silanated; I-sil/heat: I/silanated heated to 100°; P-sil/heat: P/silanated heated to 100°; (I: I/not silanated; and P: P/not silanated. Specimens were prepared for flexural strength(10×2×1 mm)and for compressive strength9.5×5.5×3 mm) and tested at 0.5 mm/min. Statistical analysis demonstrated the following for flexural strength(P< 0.05 ): I-sil:155.89±45.27BC; P-sil:155.89±45.27BC; I-sil/heat:130.20±22.11C; P-sil/heat:169.86±50.29AB; I:131.87±15.86C. For compressive strength, the following are demonstrated: I-sil:1367.25±188.77ab; P-sil:867.61±102.76d; I-sil/heat:1162.98±222.07c; P-sil/heat:1499.35±339.06a; and I:1245.78±211.16bc. Due to the impossibility of incorporating the stipulated amount of fiber, P group was excluded. Glass fiber treatment with heated silane enhanced flexural and compressive strength of a reinforced dental methacrylate. |