| Popis: |
Three-layer gelatin films, composed of sodium montmorillonite (MMt) – plasticized gelatin (Ge-5MMt) (inner layer) and dialdehyde starch (DAS) – cross-linked and plasticized gelatin films (Ge-10DAS) (outer layers), obtained by heat-compression molding, were submitted to degradation under indoor soil burial conditions for 14 days. Biodegradation of multilayer film as well as individual components and control gelatin films was evaluated by monitoring water absorption and weight loss. It was established that technological treatments performed on gelatin, such as cross-linking, compounding with clay and heatcompression molding have a major impact on the biodegradation rate and extent. The possible reasons are discussed. Weight loss results revealed that the susceptibility to microbial attack during soil burial varied in the order: Ge-10DAS < multilayer < Ge-5MMt < gelatin control film. The intermediate behaviour of the multilayer was associated with the presence of hydrogen-bonding interactions between layers, induced by processing. Scanning electron microscopy revealed that the multilayer was preferentially biodegraded by filamentous microorganisms and even larvae in the later stages of the process. The presence of holes and pits on the multilayer surface was more likely attributed to the preferential removal of glycerol and DAS as shown by thermogravimetric analysis Fil: Martucci, Josefa Fabiana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina |
Full Text from ScienceDirect