Polycaprolactone- Chitosan- Ag coatings on Ti6Al4V: Critical synergic aspects analyzed by Raman, EFM and contact angle
| Autor: | Hugo Armando Estupiñan-Duran, Sara Leal-Marin |
|---|---|
| Přispěvatelé: | Universidad de Antioquia |
| Jazyk: | angličtina |
| Rok vydání: | 2018 |
| Předmět: |
Materials science
Scanning electron microscope 020209 energy Electrostatic force microscope recubrimiento biocompatible Energy-dispersive X-ray spectroscopy Recubrimiento biocompatible wettability bone implant 02 engineering and technology engineering.material lcsh:Technology Contact angle symbols.namesake chemistry.chemical_compound Coating Biocompatible coating wettability electric potential polymers bone implant electric potential polímeros 0202 electrical engineering electronic engineering information engineering polymers Biocompatible coating lcsh:T General Engineering mojabilidad 021001 nanoscience & nanotechnology chemistry Chemical engineering lcsh:TA1-2040 Polycaprolactone symbols engineering Wetting potencial eléctrico implante óseo 0210 nano-technology Raman spectroscopy lcsh:Engineering (General). Civil engineering (General) |
| Zdroj: | Revista Facultad de Ingeniería Universidad de Antioquia, Issue: 89, Pages: 59-67, Published: DEC 2018 Revista Facultad de Ingeniería, Iss 89, Pp 59-67 (2018) |
| Popis: | The Ti6Al4V presented a natural oxide layer that increased the corrosion resistance of the material but decreased the physicochemical compatibility with the bone tissue. The use of polymeric coatings on Ti6Al4V allows the creation of an interface that promotes osseointegration and antibacterial activity. The objective of this work was to analyze a coating on Ti6Al4V obtained by dip-coating with a mixture of chitosan, polycaprolactone, and silver. The synergy between chitosan and silver allows the polymeric matrix to be retained and to enhance the coating’s mechanical-structural functions, integrating bone cells and serving as antibacterial agents. Coating morphology was assessed by scanning electron microscopy (SEM) and the distribution of chemical elements was determined by energy dispersive spectroscopy (EDS). Confocal Raman spectroscopy was used to evaluate the composition and structure of the coating. Electrical potential distribution, phase distribution and surface topography of surfaces were analyzed using an electrostatic force microscopy. Contact angle measurements were also performed to determine coating wettability. RESUMEN El Ti6Al4V presenta una capa pasiva de óxido natural que aumenta su resistencia a la corrosión, pero disminuye su compatibilidad fisicoquímica con el tejido óseo. Los recubrimientos poliméricos en la aleación de Ti6Al4V permiten la creación de una interface entre el tejido óseo y la aleación que promueva la osteointegración y otros efectos dependiendo de sus componentes, como la actividad antibacterial. El objetivo de este trabajo fue analizar un recubrimiento sobre Ti6Al4V obtenido por medio de dip-coating con una mezcla de quitosano, policaprolactona y plata. La sinergia entre el quitosano y la plata permitió retener la matriz polimérica y mejorar las funciones estructurales del recubrimiento, sirviendo como agente integrador de las células óseas y posible agente antibacteriano. La morfología del recubrimiento se evaluó por microscopia electrónica de barrido (MEB) y la composición elemental por espectroscopia de energía dispersiva de rayos X (EDS). Se empleó espectroscopia confocal Raman para evaluar la composición y estructura del recubrimiento. La distribución del potencial eléctrico, fase y topografía de las superficies se analizó usando microscopia de fuerzas electrostáticas. Y por último la mojabilidad de los recubrimientos se realizó con mediciones de ángulo de contacto. |