Engineering failure analysis of corroded R.C. beams in flexure and shear
| Autor: | F. Cannella, Giuseppe Campione |
|---|---|
| Přispěvatelé: | Campione, G., Cannella, F. |
| Rok vydání: | 2018 |
| Předmět: |
Materials science
Shear-moment interaction Bond strength 0211 other engineering and technologies General Engineering 020101 civil engineering Pitting 02 engineering and technology 0201 civil engineering Corrosion Cracking Engineering (all) Flexural strength Deflection (engineering) 021105 building & construction Load-deflection response Pitting corrosion General Materials Science Limit state design Materials Science (all) Slippage Composite material Bond |
| Zdroj: | Engineering Failure Analysis. 86:100-114 |
| ISSN: | 1350-6307 |
| DOI: | 10.1016/j.engfailanal.2017.12.015 |
| Popis: | In the present paper, a simple model to reproduce the load-deflection response of corroded beams failing in flexure and shear is presented and discussed. Effects of diffused and pitting corrosion on steel bars, compressive concrete strength degradation and concrete bond strength degradation due to rust formation are included in the model. Engineering approach based on limit state theory was here adopted to predict the peak and the residual flexural and shear strength of corroded beams with corresponding deflections and ductility estimation. Calculation of deflection at cracking taking into account of rust formation and deflection at yielding and the ultimate state taking into account also of slippage of steel bars due to rust formation were made. The model was also widely verified against tests available in the literature referred to crack opening, pit depth, attach corrosion penetration, load-deflection curves. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect