Impact of lignin source on the performance of thermoset resins

Autor: Iuliana Ribca, Benedikt Sochor, Marie Betker, Stephan V. Roth, Martin Lawoko, Olena Sevastyanova, Michael A.R. Meier, Mats Johansson
Jazyk: angličtina
Rok vydání: 2023
Předmět:
Zdroj: European Polymer Journal, 194, Art.-Nr.: 112141
ISSN: 0014-3057
1873-1945
DOI: 10.5445/ir/1000159091
Popis: A series of different technical hardwood lignin-based resins have been successfully synthesized, characterized, and utilised to produce thiol-ene thermoset polymers. Firstly, technical lignin was fractionated and allylated, whereafter it was crosslinked with a trifunctional thiol. Structural and morphological characteristics of the lignin fractions were studied by $^{1}$H NMR, $^{31}$P NMR, SEC, FTIR, DSC, TGA, and WAXS. The hardwood lignin fractions have a high content of C5-substituted OH groups. The WAXS studies on lignin fractions revealed the presence of two π-π stacking conformations, sandwiched (4.08–4.25 Å) and T-shaped (6.52–6.91 Å). The presence of lignin superstructures with distances/sizes between 10.5 and 12.8 Å was also identified. The curing reaction of the thermosets was investigated by RT-FTIR. Almost all thermosets (excepting one fraction) reached 95% of the thiol conversion in less than 17 h, revealing the enhanced reactivity of the allylated hardwood lignin samples. The mechanical properties of the thermosets were investigated by DMA. The curing performance, as well as the final thermoset properties, have been correlated to variations in chemical composition and morphological differences of lignin fractions. The described results clearly demonstrate that technical hardwood lignins can be utilized for these applications, but also that significant differences compared to softwood lignins have to be considered for material design.
Databáze: OpenAIRE
Externí odkaz: