Characterization of Algerian kaolins for utilization as a raw material in electrical insulators
| Autor: | M. Laraba |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2019 |
| Předmět: |
electrical insulators
Materials science Dielectric strength Scanning electron microscope Metallurgy Raw material engineering.material Halloysite Flexural strength lcsh:TA1-2040 Impurity resistência à flexão Ceramics and Composites engineering Kaolinite Djebel Debbagh kaolin bending strength lcsh:Engineering (General). Civil engineering (General) Thermal analysis isolantes elétricos dielectric strength Djebel Debbagh caulim rigidez dielétrica |
| Zdroj: | Cerâmica, Volume: 65, Issue: 374, Pages: 267-273, Published: 06 JUN 2019 Mohammed Laraba Cerâmica v.65 n.374 2019 Cerâmica (São Paulo. Online) Universidade de São Paulo (USP) instacron:USP Cerâmica, Vol 65, Iss 374, Pp 267-273 |
| Popis: | The aim of this investigation was to characterize three samples of kaolin (DD1, DD2 and DD3) collected from Djebel Debbagh deposit (East of Algeria) to be used in electrical porcelain insulators. Grain-size analysis, X-ray fluorescence, X-ray diffraction, scanning electron microscopy and thermal analysis (TG-DTA) were performed. Each sample was mixed with feldspar and silica to obtain three porcelain formulations. The obtained results indicated that the three kaolins were composed by kaolinite and halloysite with variable contents of MnO and Fe2O3 as associated impurities. It was found that the DD1 was the appropriate kaolin as raw material for making the high-voltage electrical insulator which had the highest electrical and mechanical properties (dielectric strength, bending strength and bulk density), while DD2 and DD3 were less suitable due to their lower properties caused by the presence of impurities which must be removed. Resumo O objetivo desta investigação foi caracterizar três amostras de caulim (DD1, DD2 e DD3) coletadas do depósito de Djebel Debbagh (leste da Argélia) para serem utilizadas em isoladores elétricos de porcelana. Análise granulométrica, fluorescência de raios X, difração de raios X, microscopia eletrônica de varredura e análise térmica (TG-ATD) foram realizadas. Cada amostra foi misturada com feldspato e sílica para obter três formulações de porcelana. Os resultados obtidos indicaram que os três caulins foram compostos por caulinita e haloisita com teores variáveis de MnO e Fe2O3 como impurezas associadas. Verificou-se que o DD1 foi o caulim adequado como matéria-prima para a fabricação do isolante elétrico de alta tensão que apresentou as maiores propriedades elétricas e mecânicas (rigidez dielétrica, resistência à flexão e densidade aparente), enquanto DD2 e DD3 foram menos adequados devido às suas propriedades inferiores causadas pela presença de impurezas que devem ser removidas. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|