Effective Propagation of HPAM Solutions Through the Tambaredjo Reservoir During a Polymer Flood
| Autor: | Ludwig Gil, Kathleen Priscilla Moe Soe Let, Randall S. Seright, Bernard Quillien, Renuka Natalie Manichand |
|---|---|
| Rok vydání: | 2013 |
| Předmět: |
chemistry.chemical_classification
Materials science Petroleum engineering Polyacrylamide Energy Engineering and Power Technology Polymer Total dissolved solids Salinity Viscosity chemistry.chemical_compound Fuel Technology Polymer degradation Rheology chemistry Polymer flood Composite material Porous medium |
| Zdroj: | All Days. |
| DOI: | 10.2118/164121-ms |
| Popis: | Summary Two new methods were developed for anaerobically sampling polymer solutions from production wells in the Sarah Maria polymer-flood-pilot project in Suriname. Whereas previous methods indicated severe polymer degradation, the improved methods revealed that the polymer propagated intact more than 300 ft through the Tambaredjo formation. Our results may help explain the inconsistency between good production responses and highly degraded polymer observed in many past field projects. Analysis of produced salinity, polymer concentration, and viscosity indicated that the polymer banks retained low salinity and, therefore, high viscosity for much of the way through the Sarah Maria polymer-flood-pilot pattern. A strong shear-thickening rheology was observed for 1,000 ppm and 1,350 ppm hydrolyzed polyacrylamide (HPAM) solutions in porous media, even though the salinity was only 500 ppm total dissolved solids (TDS). Examination of injectivities revealed that these solutions were injected above the formation parting pressure in the Sarah Maria polymer-injection wells. Injectivity was insufficient until fractures were initiated hydraulically; however, the fractures propagated a distance of only approximately 20 ft and did not jeopardize sweep efficiency. In contrast, the short fractures greatly improved polymer injectivity and reduced concern about polymer mechanical degradation. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|