Hydrolytic stability of silanated zirconia-silica-urethane dimethacrylate composites
Autor: | N. M. Mohsen, Robert G. Craig |
---|---|
Rok vydání: | 1995 |
Předmět: |
Analysis of Variance
Materials science Hydrolysis Polyurethanes Dental Bonding Water sorption Silanes Silicon Dioxide Composite Resins Silane Absorption chemistry.chemical_compound Acrylates Drug Stability chemistry Materials Testing Ultimate tensile strength Methacrylates Zirconium Urethane dimethacrylate Composite material General Dentistry Zirconia silica |
Zdroj: | Journal of Oral Rehabilitation. 22:213-220 |
ISSN: | 1365-2842 0305-182X |
DOI: | 10.1111/j.1365-2842.1995.tb01566.x |
Popis: | SUMMARY The effect of the method of silanation of zirconia-silica hy 3-methacrylox ypropyItrimethoxysilane (MAPM) and 3-acryloxypropyltrimethoxysilane (APM) on the diametral tensile and transverse strength of composites made from these silanated fillers and a urethane dimethacrylate was determined after 0-lOSh of hoiling in water. The water sorption of these composites was also measur-?d at times up to 108 h. Silanation with either silane significantly increased the tensile and transverse strengths and decreased water sorption relative to comparable unsilanated controls. Silanation with MAPM from ethaaol solution at three times the minimum uniform coverage gave the best overall results, and the tensile strength tests appeared to be most predictive of effectiveness of the silane treatments. |
Databáze: | OpenAIRE |
Externí odkaz: |