Sol-gel powder synthesis in the TiO2-TeO2-ZnO system: Structural characterization and properties
| Autor: | Reni Iordanova, A. Bachvarova-Nedelcheva, R. Gegova, Krassimir L. Kostov |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2020 |
| Předmět: |
Anatase
crystallization General Chemical Engineering Analytical chemistry 02 engineering and technology 010402 general chemistry 01 natural sciences lcsh:Chemistry X-ray photoelectron spectroscopy XPS Sol-gel Chemistry General Chemistry 021001 nanoscience & nanotechnology Telluric (VI) acid 0104 chemical sciences Amorphous solid Chemical state Absorption edge Polymerization lcsh:QD1-999 Rutile IR 0210 nano-technology Crystallization |
| Zdroj: | Arabian Journal of Chemistry, Vol 13, Iss 9, Pp 7132-7146 (2020) |
| ISSN: | 1878-5352 |
| Popis: | The present study deals with the gel formation tendency in the ternary TeO2-TiO2-ZnO system. Depending on the TiO2 amount, the gelation occurred at different times and subsequently several gel formation regions have been determined. Homogeneous, transparent and monolithic gels were obtained using combination of organic and inorganic precursors during the synthesis. Using XRD analysis it was established that upon the heating composites were obtained which contain an amorphous phase and different crystalline phases: TiO2 (anatase), TiO2 (rutile), α-TeO2 and ZnTeO3, depending on composition. The IR results showed that the short range order of the amorphous phases which are part of the composite materials consist of TiO6, ZnO4 and TeO4 structural units. Using UV–Vis spectroscopy it was established that the absorption edge of the gels varied from 330 nm to 364 mm and the increase in TiO2 content caused a red shifting of the cut-off. The calculated Eg values are in the range 3.41–3.75 eV higher than that of pure TiO2, TeO2 and ZnO oxides. The XPS results showed that the Te atoms in the surface layers of the samples studied exist in several chemical states as Te2+, Te0, but Te6+ dominates. Octahedrally coordinated Ti4+ ions are observed in the gels and in the samples annealed at 200 °C but a small amount of tetrahedrally coordinated Ti4+ is also detected, which indicates the incomplete polymerization of TiO6 units. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|