Calcium hydroxide influence in autogenous self-healing of cement-based materials in various environmental conditions
| Autor: | Vanessa Giaretton Cappellesso, Denise Carpena Coitinho Dal Molin, Deividi Maurente Gomes da Silva, Angela Borges Masuero, Maurício Germano Lopes Garcia |
|---|---|
| Přispěvatelé: | Comissão de aperfeiçoamento de pessoal de nível superior, Laboratório de Materiais e Tecnologia do Ambiente Construído, Universidade Federal do Rio Grande do Sul |
| Jazyk: | angličtina |
| Rok vydání: | 2021 |
| Předmět: |
Cement
Calcium hydroxide Cracks Chemistry Geography Planning and Development Metallurgy Civil construction Autogenous Self-healing Cement-based materials technology industry and agriculture Calcium hydroxide content Self-healing Environmental exposure Pozzolan equipment and supplies law.invention Autocicatrização Portland cement chemistry.chemical_compound Cracking Ambientes de exposição law Environmental conditions Mortar Shrinkage Conteúdo de hidróxido de cálcio |
| Zdroj: | Ambiente Construído v.21 n.2 2021 Ambiente construído Associação Nacional de Tecnologia do Ambiente Construído (ANTAC) instacron:ANTAC Ambiente Construído; v. 21, n. 2 (2021); 209-224 Ambiente Construído, Volume: 21, Issue: 2, Pages: 209-224, Published: 10 MAR 2021 |
| ISSN: | 1678-8621 1415-8876 |
| Popis: | Several factors, such as chemical shrinkage or environmental attack can produce concrete cracks. Calcium hydroxide content from the environment or cement hydration can promote the self-healing phenomenon (SHP). This study evaluates the calcium hydroxide concentration influence on the self-healing phenomenon of cement-based materials. Cracked mortars with different types of cement, such as a filler, pozzolanic, and high initial strength, were exposed to four environmental conditions. Titration was the method proposed to determine the amount of calcium hydroxide content leached in the water, and the cracks closure were analyzed by optical microscopy. CPII F (Portland Cement, type II, compound with limestone) samples showed no trend to Ca(OH)2 leached, and to superficial cracking closure. Regarding CPV (Portland cement, type V, high initial strength cement) samples, their behavior showed the highest Ca(OH)2 content to all environmental exposure, and cracking closure to samples in submerged condition. Thus, a significant influence in the cracks´ closure regarding the presence of Ca2+ leached to the exposure environments, and a water source related to this behavior seems to be a primary factor to improve the SHP. Resumo Diversos fatores, como retração química ou ataques ambientais podem produzir fissuras no concreto. O teor de hidróxido de cálcio do meio ambiente ou a hidratação do cimento podem promover o fenômeno de autocicatrização (SHP). Este estudo avalia a influência da concentração de hidróxido de cálcio no fenômeno de autoicatrização de materiais à base de cimento. Argamassas fissuradas com diferentes tipos de cimento, com filler calcário, pozolânico e alta resistência inicial, foram expostas a quatro condições ambientais. A titulação foi o método proposto para determinar a quantidade de hidróxido de cálcio lixiviado na água, e o fechamento das fissuras foi analisado por microscopia óptica. As amostras contendo CPII F não apresentaram tendência à lixiviação de Ca(OH) 2 e à colmatação das fissuras. Quanto às amostras com CPV, foi constatado o maior teor de Ca (OH) 2 lixiviado para todas as exposições ambientais, e um acentuado fechamento das fissurasnas amostras submersas. Dessa forma, constata-se uma influência significativa no SHP frente à uma fonte de umidade e ao conteúdo de Ca 2+ nos ambientes de exposição. |
| Databáze: | OpenAIRE |