Dissociation of c dislocations in sillimanite Al2SiO5
| Autor: | Jacques Paquet, Alain Lefebvre |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 1983 |
| Předmět: | |
| Zdroj: | Périodiques Scientifiques en Édition Électronique. |
| Popis: | c dissociated dislocations with variable dissociation widths (from 300 Å to a few microns) are systematically found in sillimanite studied by transmission electron microscopy. The corresponding stacking faults (with displacement vector 1/2 [001]) only slightly alter the anionic sublattice of the structure but they modify the order of Al and Si cations among the tetrahedral interstices ; the resulting degree of disorder depends on the orientation and the location of the faults in the structure. The observed (hk 0) preferred orientations of the faults tend to minimize the disorder, but this disorder should not be ignored as it may have significant effects on phase relations of the Al₂SiO₅ polymorphs. L'étude en microscopie électronique de la sillimanite montre la présence systématique de dislocations c dissociées avec des largeurs de dissociation très variables (de 300 Å à quelques microns). Les fautes d'empilement correspondantes, de vecteur-déplacement 1/2 [001], laissent pratiquement invariant le sous-réseau anionique de la structure mais elles modifient l'ordre Al-Si des sites tétraédriques ; le degré de désordre qui en résulte dépend de l'orientation et de la localisation des fautes dans la structure et il tend à être minimisé par l'orientation préférentielle (hk 0) de ces fautes. Cependant ce désordre ne saurait être négligé dans la mesure où il peut avoir une influence sur les transitions de phase entre polymorphes du composé Al₂SiO₅. Lefebvre Alain, Paquet Jacques. Dissociation of c dislocations in sillimanite Al2SiO5. In: Bulletin de Minéralogie, volume 106, 3, 1983. pp. 287-292. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|