Bonding Effectiveness of Universal Adhesive to Intracoronal Bleached Dentin Treated with Sodium Ascorbate
| Autor: | Thaís Fantinato Trindade, Walter Raucci Neto, Vivian Colucci, Danielle Cristine Furtado Messias, Luana Kelle Batista Moura |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
Sodium ascorbate
adhesiveness 02 engineering and technology Dental bonding Ascorbic Acid dentin 03 medical and health sciences chemistry.chemical_compound 0302 clinical medicine Adhesives Materials Testing Dentin medicine Animals Composite material Hydrogen peroxide General Dentistry Bond strength Dental Bonding 030206 dentistry tooth bleaching 021001 nanoscience & nanotechnology Ascorbic acid Shear bond medicine.anatomical_structure chemistry Cattle Adhesive 0210 nano-technology Nuclear chemistry |
| Zdroj: | Brazilian Dental Journal v.27 n.3 2016 Brazilian Dental Journal Fundação Odontológica de Ribeirão Preto (FUNORP) instacron:FUNORP Brazilian Dental Journal, Volume: 27, Issue: 3, Pages: 303-308, Published: JUN 2016 |
| ISSN: | 1806-4760 |
| Popis: | This study evaluated the effect of restorative protocol with sodium ascorbate on the shear bond strength (SBS) of a universal adhesive to intracoronal bleached dentin. One hundred-and-twenty bovine dentin fragments were randomly divided into 12 groups (n=10), according to the bleaching procedure (unbleached and bleached) and restorative protocol (no treatment, 10% sodium ascorbate -10SA, 35% sodium ascorbate -35SA and two-step etch-and-rinse -ER or one-step self-etch -SE Scotchbond universal adhesive approaches). Four whitening sessions were performed using 35% hydrogen peroxide. The samples from control groups were kept in relative humidity at 37 °C. Immediately after bleaching procedures, the assigned antioxidant solution was applied on dentin and restorative procedures were performed following either the ER or the SE approach. After 24 h, the specimens were subjected to SBS test. Data (MPa) were analyzed by ANOVA and Tukey's test (?=0.05). Lower SBS values were found for bleached specimens (8.54 MPa) compared with those unbleached (12.13 MPa) (p0.05). It may be concluded that bond strength of composite resin to intracoronal dentin was affected by restorative protocol and reduced by bleaching. Resumo Este estudo avaliou o efeito do protocolo restaurador empregando ascorbato de sódio na resistência ao cisalhamento do adesivo universal à dentina intracoronária clareada. Cento e vinte fragmentos de dentina bovina foram aleatoriamente divididos em doze grupos (n=10), de acordo com o procedimento clareador (clareados e não clareados) e protocolo restaurador (sem tratamento, ascorbato de sódio 10% (10AS), ascorbato de sódio (35AS) e estratégia de condicionamento total de dois passos (ER) ou estratégia autocondicionante de um passo (SE) com o sistema adesivo Scotchbond universal. Quatro sessões de clareamento foram realizadas empregando peróxido de hidrogênio a 35%. Os espécimes do grupo controle foram mantidos em umidade relativa a 37 °C. Imediatamente após os procedimentos de clareamento, as soluções antioxidantes selecionadas foram empregadas na dentina e os procedimentos restauradores foram realizados seguindo as estratégias ER ou SE. Após 24 h, os espécimes foram submetidos ao teste de resistência ao cisalhamento. Os dados (MPa) foram analisados pela ANOVA e teste de Tukey (?=0,05). Os menores valores de resistência ao cisalhamento foram encontrados para os espécimes clareados (8,54 MPa) comparados com aqueles não clareados (12,13 MPa) (p0,05). Pode ser concluído que a resistência de união da resina composta à dentina intracoronária foi afetada pelo protocolo restaurador e reduzida pelo clareamento. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|