Thermal radical polymerization of Bis(methacrylamide)s
| Autor: | Vicente Castelo Branco Leitune, Cesar Liberato Petzhold, Fabrício Mezzomo Collares, Douglas Gamba, Stéfani Becker Rodrigues |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2019 |
| Předmět: |
synthesis
differential scanning calorimetry (DSC) Organic Chemistry Radical polymerization Infrared spectroscopy Methacrylic anhydride Carbon-13 NMR lcsh:Chemical technology monomers chemistry.chemical_compound Monomer chemistry kinetics Diamine Polymer chemistry Proton NMR Chemical Engineering (miscellaneous) Methacrylamide lcsh:TP1-1185 adhesives |
| Zdroj: | Polímeros, Volume: 29, Issue: 2, Article number: e2019023, Published: 27 JUN 2019 Polímeros v.29 n.2 2019 Polímeros (São Carlos. Online) Associação Brasileira de Polímeros (ABPol) instacron:ABPO Polímeros, Vol 29, Iss 2 |
| Popis: | Methacrylamides monomers for dental applications were synthesized using a one-step procedure starting from methacrylic anhydride and the respective diamine: N,N’-(propane-1,3-diyl)-bis(N-ethyl-2-methylacrylamide) (1), N,N’-(butane-1,4-diyl)-bis(2-methacrylamide) (2), N,N’-(octane-1,8-diyl-)bis(2-methylacrylamide) (3) and N,N’-(1,4-phenylene)-bis(2-methylacrylamide) (4). The structures were confirmed by 1H NMR, 13C NMR, FTIR-ATR and UHPLC-QTOF-MS. Thermal polymerization kinetics was investigated by modulated DSC for monomers (2), (3) and (4) using heating rates of 1, 2, 3 and 5 °C min-1. All IR spectra showed the C=C axial deformation at 1610 cm-1, in 1H NMR spectra the olefinic hydrogens were observed at 5.3 an 5.8 ppm and in 13C NMR, the vinylic carbons at 120 and 140 ppm. The exact m/z values were: 267.2068, 225.1595, 281.2222 and 245.1283 for monomers (1), (2), (3) and (4), respectively. The activation energy was: -182.7; -165.8 and -156.7 kJ mol-1 for monomers (2), (3) and (4), respectively. Monomers are promising candidates for use as hydrolytic stable adhesive systems for dental applications. |