Development of rapid-hardening ultra-high strength cementitious composites using superzeolite and N-C-S-H-PCE alkaline nanomodifier
| Autor: | Myroslav Sanytsky, Iryna Нeviuk, Pawel Sikora, Tetiana Kropyvnytska, Serhii Braichenko |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2021 |
| Předmět: |
alkaline nanomodifier
Materials science Applied Mathematics Mechanical Engineering high temperatures Energy Engineering and Power Technology Cementitious composite HD2321-4730.9 superzeolite Industrial and Manufacturing Engineering Computer Science Applications Control and Systems Engineering Management of Technology and Innovation Hardening (metallurgy) T1-995 Industry Electrical and Electronic Engineering Composite material Technology (General) operational properties ultra-high strength cementitious composite |
| Zdroj: | Eastern-European Journal of Enterprise Technologies, Vol 5, Iss 6 (113), Pp 62-72 (2021) |
| Popis: | It is shown that high operational reliability of structural materials, in particular at high temperatures, is achieved through the use of ultra-high strength cement composites. Studies of various types of Portland cements with mineral additives of the CEM II/A type have established that a stone based on Portland cement with superzeolite is the most resistant to high temperatures. It has been proven that due to the "self-autoclaving" effect, the strength of a stone based on CEM II/A-P 42.5 R is 1.2–1.3 times higher than a stone based on other types of CEM II/A. To obtain fast-hardening cement composites, a nanotechnological approach based on the use of sol-gel technology has been implemented. Using the methods of IR spectroscopy, electron microscopy, the fact of obtaining, by the chemical method of synthesis, an alkaline nanomodifier N-C-S-H-PCE, which is a nano–liquid based on nano-core seeds of sodium/calcium hydrosilicates, has been proved. It has been confirmed that the introduction of the alkaline nanomodifier N-C-S-H-PCE provides a significant intensification of the early structure formation processes in the paste based on Portland cement with superzeolite (after 12 hours, 24 hours and 28 days, the strength is 16.9; 30.5 and 104.1 MPa). It has been established that the complex combination of Portland cement with superzeolite, corundum aggregate, basalt fiber and alkaline nanomodifier provides rapid-hardening of ultra-high strength cement composites (T=400 °C) with improved operational properties. Thus, there is reason to assert the feasibility of developing rapid-hardening ultra-high strength cementitious composites. This solves the problems associated with the need to increase their early strength and performance. As a result, it is possible to carry out repair work to protect equipment from abrasive wear at elevated temperatures |