Characterization of pervious concrete focusing on non-destructive testing
| Autor: | S. T. MARTINS FILHO, E. M. BOSQUESI, J. R. FABRO, R. PIERALISI |
|---|---|
| Rok vydání: | 2020 |
| Předmět: |
porosity
Materials science Pervious concrete pervious concrete 0211 other engineering and technologies 020101 civil engineering 02 engineering and technology porosidade 0201 civil engineering 021105 building & construction Ultimate tensile strength Composite material Porosity Cement Building construction Aggregate (composite) permeabildiade General Medicine compressive strength concreto permeável resistência à compressão Permeability (earth sciences) Compressive strength ultrasound method Ultrasonic sensor permeability TH1-9745 método do ultrassom |
| Zdroj: | Revista IBRACON de Estruturas e Materiais, Volume: 13, Issue: 3, Pages: 483-500, Published: 13 JUL 2020 Revista IBRACON de Estruturas e Materiais v.13 n.3 2020 Revista IBRACON de Estruturas e Materiais Instituto Brasileiro do Concreto (IBRACON) instacron:IBRACON Revista IBRACON de Estruturas e Materiais, Vol 13, Iss 3, Pp 483-500 (2020) |
| ISSN: | 1983-4195 |
| DOI: | 10.1590/s1983-41952020000300003 |
| Popis: | This study aims to investigate the properties of pervious concrete focusing on characterization tests by the Ultrasound Method. For this, three mixtures were produced with the paste/aggregate (P/Ag) ratio ranging from 0.45 to 0.65, water to cement ratio (w/c) of 0.3, and all the specimens were compacted with a steel rod. The application of the ultrasound method deserves special attention for the characterization of pervious concrete, due to a lack of research and the potential to develop analytical models for predicting properties from ultrasonic pulse velocity (UPV) as an independent variable. The UPV obtained in this study ranged from 3642 to 4262 m/s for an approximately 12% reduction in porosity, with a correlation (R²) of 0.91. It is noteworthy that the high porosity of pervious concrete causes attenuation of the ultrasonic wave. The measurements of UPV had higher values for specimens with higher densities (R²=0.87), higher compressive and tensile strengths (R² of 0.79 and 0.84, resp.), and lower permeability (R² = 0.91). Resumo Neste estudo, objetiva-se investigar as propriedades do concreto permeável com foco nos ensaios de caracterização pelo Método do Ultrassom. Para isso, foram produzidos três traços com a relação pasta/agregado variando de 0,45 a 0,65, relação a/c de 0,3 e compactados por haste. A aplicação do Método do Ultrassom merece atenção especial para caracterização do concreto permeável, com carência de pesquisas e com potencial de desenvolver modelos analíticos de previsão das propriedades a partir da velocidade de pulsos ultrassônicos (VPU) como uma variável independente. A VPU variou de 3642 até 4262 m/s para uma redução de aproximadamente 12% na porosidade, com alta correlação (R²) de 0,91 e destaca-se que a alta porosidade do concreto provoca atenuação da onda ultrassônica. As medições da VPU retrataram valores maiores para os CPs com maiores densidades (R²=0,87), maiores resistências à compressão e à tração (R² de 0,79 e 0,84, resp.), e menores permeabilidades (R²=0,91). |