Influence of the spray pyrolysis seeding and growth parameters on the structure and optical properties of ZnO nanorod arrays

Autor: Marchi, María Claudia, Candal, Roberto J., Rodríguez, Juan, Feuillet, Guy, Donatini, Fabrice, Onna, Diego, Sanchez, Luis, Bilmes, Sara A., Chandezon, Frédéric
Přispěvatelé: Universidad Nacional de Ingeniería (UNI), Commissariat à l'énergie atomique et aux énergies alternatives - Laboratoire d'Electronique et de Technologie de l'Information (CEA-LETI), Direction de Recherche Technologique (CEA) (DRT (CEA)), Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Commissariat à l'énergie atomique et aux énergies alternatives (CEA), Optique et microscopies (POM), Institut Néel (NEEL), Université Joseph Fourier - Grenoble 1 (UJF)-Institut polytechnique de Grenoble - Grenoble Institute of Technology (Grenoble INP )-Centre National de la Recherche Scientifique (CNRS)-Université Joseph Fourier - Grenoble 1 (UJF)-Institut polytechnique de Grenoble - Grenoble Institute of Technology (Grenoble INP )-Centre National de la Recherche Scientifique (CNRS), Universidad de Buenos Aires [Buenos Aires] (UBA), Laboratoire d'Electronique Moléculaire Organique et Hybride (LEMOH), SYstèmes Moléculaires et nanoMatériaux pour l’Energie et la Santé (SYMMES), Institut de Chimie du CNRS (INC)-Université Grenoble Alpes [2016-2019] (UGA [2016-2019])-Institut de Recherche Interdisciplinaire de Grenoble (IRIG), Direction de Recherche Fondamentale (CEA) (DRF (CEA)), Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Direction de Recherche Fondamentale (CEA) (DRF (CEA)), Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Centre National de la Recherche Scientifique (CNRS)-Institut de Chimie du CNRS (INC)-Université Grenoble Alpes [2016-2019] (UGA [2016-2019])-Institut de Recherche Interdisciplinaire de Grenoble (IRIG), Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Centre National de la Recherche Scientifique (CNRS), Optique & Microscopies (NEEL - POM), Institut de Chimie du CNRS (INC)-Centre National de la Recherche Scientifique (CNRS)-Université Grenoble Alpes [2016-2019] (UGA [2016-2019])-Institut de Recherche Interdisciplinaire de Grenoble (IRIG), Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Commissariat à l'énergie atomique et aux énergies alternatives (CEA)-Institut de Chimie du CNRS (INC)-Centre National de la Recherche Scientifique (CNRS)-Université Grenoble Alpes [2016-2019] (UGA [2016-2019])-Institut de Recherche Interdisciplinaire de Grenoble (IRIG)
Rok vydání: 2015
Předmět:
Zdroj: Materials Chemistry and Physics
Materials Chemistry and Physics, Elsevier, 2015, 151, pp.378-384. ⟨10.1016/j.matchemphys.2014.12.013⟩
Universidad Nacional de Ingeniería
Repositorio Institucional-UNI
UNI-Tesis
instacron:UNI
Materials Chemistry and Physics, 2015, 151, pp.378-384. ⟨10.1016/j.matchemphys.2014.12.013⟩
ISSN: 0254-0584
DOI: 10.1016/j.matchemphys.2014.12.013
Popis: ZnO nanorods (NRs) were grown on fluorine doped tin oxide (FTO) substrates at low temperatures (90 °C) from Zn2+ precursors in alkaline media previously seeded with ZnO nanoparticles. These were deposited onto the FTO substrate heated at 350 °C by spray pyrolysis of a Zn acetate solution in a water ethanol mixture. The structure of seeds was tuned by the ethanol to water ratio, Γ, which controls the solvent evaporation rate of drops impinging the substrate. From a detailed characterization using a combination of scanning electron microscopy, X-ray diffraction, UV-visible absorption and cathodoluminescence spectroscopies, the dependence of the morphology and optical properties of the ZnO NRs on the seeding conditions was demonstrated. NRs grown on seeds deposited from solutions with Γ in the 0.03-0.06 range - i.e. when the surface excess of ethanol in the water-ethanol mixture has a maximum - show thinner average diameters and stacking faults due to the presence of zinc blende domains embedded into an overall wurtzite NR. They furthermore exhibit blue-shifted near band edge emission peak and a high deep level emission in cathodoluminescence. All these findings support the use of spray pyrolysis as a simple and reproducible way to control the seeds deposition, influencing the growth, the structure and the optical properties of the final ZnO NRs. Fil: Rodríguez, Juan. Universidad Nacional de Ingeniería; Perú Fil: Feuillet, Guy. CEA Grenoble; Francia Fil: Donatini, Fabrice. Université Grenoble Alpes; Francia. Centre National de la Recherche Scientifique. Institut Néel; Francia Fil: Onna, Diego Ariel. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina Fil: Sanchez, Luis. Universidad Nacional de Ingeniería; Perú Fil: Candal, Roberto Jorge. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad Nacional de San Martín. Instituto de Investigación e Ingeniería Ambiental; Argentina Fil: Marchi, María Claudia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Centro de Microscopías Avanzadas; Argentina Fil: Aldabe, Sara Alfonsina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina Fil: Chandezon, Frédéric. Université Grenoble Alpes; Francia. Centre National de la Recherche Scientifique; Francia