MODELING OF CONTROLLED MOVEMENT OF THE INDENTOR WHILE MEASURING THE HARDNESS OF THE DETAIL’S MATERIAL

Autor: Gregory S. Tymchik, Volodymyr Skytsiouk, Michael Bulyk, Tatiana Klotchko, Myroslava Pechonka
Rok vydání: 2018
Předmět:
Zdroj: Вісник Національного технічного університету України "Київський політехнічний інститут". Серія Приладобудування; № 55(1) (2018); 81-88
Вестник Национального технического университета Украины "Киевский политехнический институт". Серия приборостроение; № 55(1) (2018); 81-88
Bulletin of National Technical University of Ukraine "Kyiv Polytechnic Institute". Series Instrument Making; № 55(1) (2018); 81-88
ISSN: 2663-3450
0321-2211
DOI: 10.20535/1970.55(1).2018.135904
Popis: Introduction. The article deals with the actual problem of measuring the hardness parameters of various parts of the material, which are designed to work under conditions of high loads, as well as in the manufacture of artificial implants intended for introduction into the living body and functioning for a very long time. This creates additional requirements for the quality of these parts. Currently, there are development tools for measuring the value of microhardness, however, they are either not intended for use on machines, or portable devices can not withstand the necessary accuracy.Main part. The problem of determining the moment of contact of the indenter with the surface of the part and the speed of motion of the indenter when measuring the hardness and microhardness of the material of the parts is considered.the result gives a description of two possible cases in determining the hardness of materials.The first expression refers to the case when the loading speed is large enough. In the second case, we have a gradual load, which differs from the previous case. After accepting these conditions, we obtain the result, which proves the dependence of the speed of the indenter of the rigid meter on the nature of the pressure.If we do a comparative analysis of the velocities, then we get the following result. Since the speed in the first case is much higher, then some conditions need to be taken to solve this problem.A model is created for the transient process of pressure growth, formed during measurement and depends on the type of load. In further studies, it is advisable to continue the analysis of the motion of the indenter when testing for hardness of materials.Conclusion. To do this, we will further analyze the model for determining the moment of contact of the indenter with the surface of the workpiece, affecting the accuracy of measuring the hardness parameters of the material of the workpiece.
У статті йдеться про актуальну проблему вимірювання параметрів твердості матеріалу деталей різного призначення, які призначені для роботи в умовах великих навантажень, а також при виготовленні штучних імплантів, що призначені для вживлення у живий організм та функціонування їх протягом дуже тривалого часу. Це створює додаткові вимоги до якості цих деталей.Розглянуто проблему визначення моменту торкання індентора до поверхні деталі та швидкості руху індентора під час вимірювання твердості та мікротвердості матеріалу деталей. Створено модель перехідного процесу зростання тиску, що утворюється при вимірюванні та залежить від типу навантаження. У подальших дослідженнях доцільно продовжити аналіз руху індентора під час випробування на твердість матеріалів. Для цього у подальшому проаналізуємо модель визначення моменту торкання індентора до поверхні деталі, що впливає на точність вимірювання параметрів твердості матеріалу деталі.