Effect of Ag Underlayer on Microstructures and Perpendicular Magnetic Properties of CoPt Nanocomposite Thin Films
| Autor: | Po-Cheng Kuo, S.C. Chen, Huang Kt, Chi-Kai Shen, Lin Gp, Yang Li, S.L. Ou |
|---|---|
| Rok vydání: | 2011 |
| Předmět: |
Materials science
Condensed matter physics Annealing (metallurgy) Perpendicular magnetic anisotropy Biomedical Engineering Bioengineering Nanocomposite thin films General Chemistry Coercivity Sputter deposition Condensed Matter Physics Microstructure Perpendicular General Materials Science Single layer |
| Zdroj: | Journal of Nanoscience and Nanotechnology. 11:11171-11175 |
| ISSN: | 1533-4880 |
| DOI: | 10.1166/jnn.2011.4044 |
| Popis: | CoPt/Ag films were prepared by magnetron sputtering on glass substrates and subsequent annealing. The dependence of degree of ordering and magnetic properties on Ag film thickness and annealing conditions were investigated. It was found that the Ag underlayer played a dominant role in inducing the (001) texture of the CoPt film after annealing. CoPt films with a thickness about 20 nm and Ag underlayers with a thickness about 70 nm are easy to obtain a large degree of ordering and a perpendicular magnetic anisotropy after annealing at 700 degrees C for 30 min. CoPt/Ag films with out-of-plane coercivity (Hc (perpendicular)) in the range of 13.5-14.0 kOe and a out-of-plane squareness (S(perpendicular)) of 0.97 were obtained after annealing at 700 degrees C for 30 min. Ag underlayer is beneficial to enhance the Hc(perpendicular)and S(perpendicular) of CoPt film significantly. The degree of ordering and perpendicular magnetic properties of the CoPt films which deposited on Ag underlayer are larger than those of the single layer CoPt films. |