Improvement of β-Ga2O3 MIS-SBD Interface Using Al-Reacted Interfacial Layer
| Autor: | Lingli Jiang, Hongyu Yu, Minghao He, Kah-Wee Ang, Fanming Zeng, Wei-Chih Cheng, Qing Wang, Yang Jiang, Wenmao Li, Zepeng Qiao, Yu-Chieh Chien |
|---|---|
| Rok vydání: | 2021 |
| Předmět: | |
| Zdroj: | IEEE Transactions on Electron Devices. 68:3314-3319 |
| ISSN: | 1557-9646 0018-9383 |
| Popis: | In this article, a $\beta $ -Ga2O3 metal-interlayer-semiconductor Schottky barrier diode (MIS-SBD) using Al-reacted aluminum oxide as the interlayer is demonstrated for the first time and compared with conventional metal-semiconductor (MS) Schottky barrier diode (SBD). The aluminum oxide is formed by sputtering a thin Al layer on Ga2O3 substrate and then annealed in O2 at 300 °C. With the insertion of Al-reacted interlayer, the SBD subthreshold swing (SS) is significantly improved to 61 mV/dec with an average current range of >6 orders. Example of atomic layer deposited (ALD) Al2O3 as the interlayer is also fabricated and characterized. ${J}$ – ${V}$ study corrected by Gaussian distribution model shows that all the samples statistically exhibit similar mean barrier heights (BHs). This indicates that the interlayer hardly affects the electrostatic field and band bending as experienced by carrier injections. ${C}$ – ${V}$ study provides different BH results in different sample setups. The result proves that Al-reacted interfacial layer helps eliminate interface degradation as compared with ALD Al2O3. Overall, MIS-SBD by Al-reaction method exhibits improved SS, reduced reverse leakage current ( ${I}_{0}$ ), low ideality factor, good ON-OFF ratio ( $> 10^{9}$ ), and minimized interface charges as compared with its respective counterparts. The result of this article serves as a promising interface engineering technique for Ga2O3-based SBD designs. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|