| Autor: |
R. Menon, T W Crooker, J A Hauser, S J Gill, B.J. Kruse, C.D. Lundin |
| Rok vydání: |
2009 |
| Předmět: |
|
| DOI: |
10.1520/stp23288s |
| Popis: |
The applicability of linear elastic fracture mechanics to characterize the fatigue behavior of high-strength steel weldments containing lack-of-penetration (LOP) and slag/lack-of-fusion (S/LOF) discontinuities is explored. Full penetration, double-V butt welds with reinforcements removed were tested under zero-to-tension axial loading. Various filler metals and welding techniques were used. Both sound welds and welds containing discontinuities were cycled to failure. Where possible, cycles to crack initiation were estimated by strain gage measurements. The fracture mechanics approach was successful in correlating the fatigue lifetimes of specimens containing single LOP discontinuities of varying size. However, the fatigue behavior of specimens containing multiple S/LOF discontinuities proved to be much more complex and difficult to analyze. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|