Differently sintered TiOx hole blocking layers for solution processed solar cells
| Autor: | Miroslav Mikolášek, Milan Mikula, Jarmila Müllerová, Pavol Gemeiner, Michal Hatala, Matej Hvojnik, Zuzana Beková, Matej Jergel |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Anatase
Materials science Band gap Annealing (metallurgy) General Physics and Astronomy chemistry.chemical_element Nanoparticle Sintering 02 engineering and technology Surfaces and Interfaces General Chemistry 010402 general chemistry 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences 0104 chemical sciences Surfaces Coatings and Films Amorphous solid law.invention chemistry Chemical engineering law Solar cell 0210 nano-technology Titanium |
| Zdroj: | Applied Surface Science. 461:54-60 |
| ISSN: | 0169-4332 |
| Popis: | Thin TiOx layers were prepared by dip-coating using titanium diisopropoxide acetylacetonate (TiAcAc) precursor on different substrates and annealed at different temperatures. Atomic force microscopy, UV–Vis, FTIR and XRD spectroscopy were used to determine thickness, morphological and structural changes with annealing temperature, including refractive index, extinction coefficient, optical band gap and removal of organic content. These differently sintered layers were used as the compact hole blocking layers in dye-sensitized and perovskite solar cells systems, keeping all other processes of cells preparation below 150 °C (including mesoporous oxides layers), simulating thus the low-T processes. Some jumps of blocking layer parameters found within sintering are related to a step increase of the efficiency of dye-senzitized cells at 150 °C, that can be useful in the low-temperature process, e.g. if TiAcAc is used as a binder of nanoparticles. However, deeper structural changes of the layers leading to higher efficiency were found out just above 350 °C. It is caused primarily by too high series resistances of low-T blocking layers that are very amorphous. So the addition of more conductive (anatase) nanoparticles into the blocking layer is much demanded. In any case, it is meaningful to use maximum acceptable temperature in the low-T process (e.g. on plastic substrates) of TiAcAc application in solar cells, where can be concluded that perovskite cells are more sensitive to defects and quality of blocking layer than dye-sensitized ones. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect