In the present work, the Y0.95Ba0.05Mn0.90Ti0.10O3 ceramic sample was prepared using a conventional solid-state reaction method, and its structural, vibrational, and ferroelectric behaviors were studied at room temperature. The XRD analysis of the prepared material confirms the hexagonal crystal structure with P63cm space group symmetry. The Rietveld refinement of the sample also justifies the results. The Raman spectroscopy reveals the subtle variation of different vibrational modes due to Ba2+ and Ti4+ ions doping at different sites. The ferroelectric measurement performed at room temperature and different voltages reveal that the material exhibits weak ferroelectricity. |