Autor: Czeslaw Slusarczyk, Grazyna Strobin, Andrzej Wlochowicz, Andrzej Dems
Rok vydání: 1988
Předmět:
Zdroj: Angewandte Makromolekulare Chemie. 156:69-77
ISSN: 1522-9505
0003-3146
DOI: 10.1002/apmc.1988.051560107
Popis: The separation of phases in defined multiblock (b-styrene-bisphenol A carbonate) copolymers was analyzed by small-angle X-ray scattering. It was found that these copolymers form typical microdomain structures. For copolymers containing 0.34 and 0.47 wt.-parts polycarbonate (PC) the microdomains are arranged in the face-centred cubic macronetwork. The distance between domains decreases with increasing concentration of polycarbonate. The copolymer containing 0.767 PC has lamellar structure. The thickness of the domain-boundary interphase was quantitatively estimated by analyzing a systematic deviation of the scattering curves at large angle tail from the Porod's law. The thickness of the transition layer decreases with increasing concentration of polycarbonate. Die Phasentrennung in definierten Multiblock(b-Styrol/Bisphenol A Carbonat) Copolymeren wurde mit Hilfe der Rontgenkleinwinkelstreuung analysiert. Es zeigte sich, das diese Copolymeren eine typische Mikrodomanenstruktur bilden. Fur Copolymere, die 0,34 und 0,47 Gew.-Teile Polycarbonat enthalten, sind die Mikrodomanen in einem flachenzentrierten kubischen Makrogitter angeordnet. Die Absttande zwischen den Domtanen nehmen mit zunehmender Konzentration von Polycarbonat ab. Das Copolymere, das 0,767 Gew.-Teile Polycarbonat enthtalt, zeigt Lamellenstruktur. Die Dicke der Grenzflachenschicht wurde quantitativ abgeschtazt durch Analyse der systematischen Abweichung der Streukurven bei grosen Winkeln vom Porodschen Gesetz. Die Dicke der Ubergangsschicht nimmt mit zunehmender Konzentration von Polycarbonat ab.
Databáze: OpenAIRE
Externí odkaz: