Void formation and filling under alumina scales formed on Fe–20Cr–5Al based alloys and coatings, oxidised at temperatures up to 1200 °C
| Autor: | M. J. Bennett, H. Al-Badairy, Gordon J. Tatlock, D. J. Potter |
|---|---|
| Rok vydání: | 2008 |
| Předmět: |
Void (astronomy)
Materials science Silicon Scanning electron microscope Mechanical Engineering Metallurgy Metals and Alloys Oxide chemistry.chemical_element General Medicine engineering.material Chromia Surfaces Coatings and Films Corrosion chemistry.chemical_compound chemistry Coating Mechanics of Materials Materials Chemistry engineering Environmental Chemistry Composite material Silicon oxide |
| Zdroj: | Materials and Corrosion. 59:414-422 |
| ISSN: | 1521-4176 0947-5117 |
| Popis: | During the oxidation, in laboratory air, of thin foils of Fe-20Cr-5Al based alloys, voids were formed in the substrate beneath the outer protective alumina scale after times varying from 50 h at 900 °C to 10 min at 1200 °C. Once the substrate aluminium level had dropped below a critical value ( |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Plný text