A numerical study of transverse cracking in cross-ply laminates by 3D finite fracture mechanics
| Autor: | Anthony R. Ingraffea, Vladislav Mantic, B.J. Carter, I.G. García |
|---|---|
| Rok vydání: | 2016 |
| Předmět: |
Optimization problem
Materials science Mechanical Engineering 02 engineering and technology 021001 nanoscience & nanotechnology Crack growth resistance curve Industrial and Manufacturing Engineering Finite fracture mechanics Stress (mechanics) Crack closure 020303 mechanical engineering & transports 0203 mechanical engineering Mechanics of Materials Position (vector) Ultimate tensile strength Ceramics and Composites Composite material 0210 nano-technology Finite set |
| Zdroj: | Composites Part B: Engineering. 95:475-487 |
| ISSN: | 1359-8368 |
| Popis: | Transverse cracking in cross-ply laminates is a key failure mechanism which needs to be understood in order to predict the failure initiation in these laminates. A new 2D model has recently been presented (Garcia et al., Int J Solids Struct 51, pp. 3844–3856, 2014) for predicting the first crack onsets in cross-ply laminates under tensile loading, which is based on the coupled criterion of the Finite Fracture Mechanics (FFM). This 2D model is able to predict a strong size effect on the critical strain leading to the first crack onsets, which agrees with some experiments found in the literature. However, some earlier studies have shown that the 3D effects can be relevant in determining the origin of the size effect found in these experiments. Therefore, a 3D application of the coupled criterion, which formulates this criterion as an optimization problem, is proposed here. The objective function to be minimized, under the stress and energy criteria described previously, is the critical strain leading to the first crack onset. The finite number of variables of the optimization define the crack geometry after its onset. Since the crack geometry is parametrized, the variables in the optimization are the parameters defining the crack geometry. The objective function is evaluated by combining FRANC3D and Abaqus. As occurs in the 2D model, the results predict the strong influence of the transverse-ply thickness on the process of transverse cracking. In particular, a slightly larger critical strain is predicted for thinner laminates. In addition, the optimal crack position also varies with the thickness: a free-edge crack onset is predicted for thick laminates, whereas for thin ones, the inside and free-edge crack positions are essentially equivalent. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect