Effect of the form of stressed state on the kinetics of damage accumulation and crack resistance of body steel 15Kh2MFA under different conditions. Communication 1. Stagewise process of steel KP60 failure
Autor: | N. G. Chausov, A. A. Lebedev, L. V. Zaisteva, A. V. Getmanchuk |
---|---|
Rok vydání: | 1993 |
Předmět: | |
Zdroj: | Strength of Materials. 25:157-162 |
ISSN: | 1573-9325 0039-2316 |
Popis: | The kinetics of body steel KP60 failure are studied in the final stages of deformation with static tension for smooth specimens and with stress concentrators. Attention is concentrated on features of the generation and start of separation macrocracks in test specimens. Common and distinctive features of damage formation in the test steel are noted taking account of the form of stressed state. |