Strain-Ageing in Silver Iodobromide

Autor: M. T. Sprackling, M. E. Bahrololoom
Rok vydání: 1986
Předmět:
Zdroj: physica status solidi (a). 96:217-224
ISSN: 1521-396X
0031-8965
Popis: Experimental results are presented for the strain-ageing of silver iodobromide (0.35 mol% AgI). At 77 K and also above about 450 K the material shows only recovery on ageing. In the tempera-ture range 273 K to about 350 K three regions of hardening are observed, two of which persist to temperatures around 375 K. The two major hardening processes have activation energies of (0.17 ± 0.01) and (0.47 ± 0.03) eV, respectively. The observations are discussed in terms of the interactions between slip dislocations and point defects in the crystal. Les resultats experimentaux sont presentes pour le veillisement par les efforts mecaniques du AgBr:I (0.35 mol% AgI). A partir d'une temperature de 77 K ainsi que d'une temperature superieure a celle d'environs 450 K, les materiaux font preuve seulement d une recuperation vis-a-vis de l'action de veillisment. Dans l'interval qui va de 273 K a qui prět 350 K on observe trois regions de durcissement, dont deux resistent a des temperatures d'environs 375 K. Les deux pro-cessus de durcissement les plus importants ont des energies d'activation respectives de (0,17 ± 0,01) et de (0,47 ± 0,03) eV. On evalue les observations dans les termes de l'interaction entre les de-placements par glicement et les defauts locaux dans le crystal.
Databáze: OpenAIRE
Externí odkaz: