Steel companies are applying Ni-B or Ni-Co alloy plating to protect the surface of Continuous casting mold, and they are using saccharin polish which causes crack on plating layer due to sulfur in saccharin. It is considered that the Ni-S compound causes the cracking and additional tensile stresses. The Ni-Mn-B ternary alloy plating was developed for suppression of crack by forming Mn-S compound before Ni-S compound is formed, but there were no domestic or international standard on the Ni-Mn-B alloy plating. Therefore, reliability evaluation standard was established to evaluate the newly developed Ni-Mn-B plating. To develop accelerating life testing method, FMEA(Failure Mode & Effective analysis) was used to analyze the cause of the main failure in plating. The Ni-Mn-B reliability standard included accelerating life test method, and it was categorized by the fundamental performance test, environment test, and accelerated life test, and was designed to guarantee 1 000 hours of B10 life with 80 % reliable level. |