| Popis: |
Micron-sized WC-CrCNi powder (WC-metal powder, WC 68%, C 0.56%, Cr 21% Ni 6%) was coated onto magnetic shaft material Inconel718 (In718) surface using HVOF thermal spraying equipment for the improvement of the surface properties of the shaft. During the HVOF coating, metal carbides, such as WC and Cr7C3 decomposed to W2C, metals and free carbon. The free carbon and the excesively sprayed oxygen formed carbon oxide gases and thus produced pores and voids in coating. The optimal coating process (OCP) that produced the lowest coating surface porosity and the highest surface hardness was determined by the Taguchi experimental program of nine processes for four spray parameters with three levels. Coatings with porosity 1.20±0.1% and hardness 1150±60 Hv were prepared using optimal coating processes. The coating was porous, but the hardness was improved approximately three times from 400±10 Hv (In718) to 1150±60 Hv (coating). Friction coefficients (FC) of the coating were lower compared with In718 at both 25°C and 450°C. FC decreased with increasing temperature from 25°C to 450°C for both In718 and the coating. Wear depths of coatings were smaller than those of In718 at both 25°C and 450°C. For the improvement of the surface properties and durability of the magnetic shaft, HVOF WC-CrCNi power coating was recommended. |