Thermodynamic features of the synthesis of high-density ceramic-metal materials 'chromium oxide–chromium' from mixtures 'chromium oxide–carbon' in the process of hot pressing
| Autor: | E. S. Gevorkyan, V. P. Nerubatskyi, R. V. Vovk, T. Szumiata, D. A. Hordiienko, M. Gzik-Szumiata |
|---|---|
| Rok vydání: | 2023 |
| Předmět: | |
| Zdroj: | Low Temperature Physics. 49:384-391 |
| ISSN: | 1090-6517 1063-777X |
| Popis: | Obtaining ceramic-metal materials Cr2O3–Cr by reduction of chromium with carbon in the process of hot pressing makes it possible to get high-density materials for various functional applications. The thermodynamical study of the interaction of chromium oxide with carbon (soot) is of particular interest, since not only reduced chromium is formed during the synthesis, but also chromium carbides with different stoichiometry, which makes it possible to increase the density and, consequently, the strength of the composite as a whole. Using the partial reduction of chromium oxide with carbon, it is possible to synthesize ceramic-metal materials “chromium oxide–chromium” with different chromium content. The degree of occurrence of this reaction depends on the content of carbon monoxide in its products by lowering the concentration of the obtained pure chromium. This method enables obtaining a ceramic-metal material Cr2O3–22 wt% Cr of eutectic composition, which is characterized by special physical and mechanical properties. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|