| Autor: | Zakhvalinskii, Vasilii, Borisenko, Alexander, Nikulicheva, Tatyana, Kochura, Alexey, Htet, Aung Zaw, Pilyuk, Evgeniy |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2022 |
| Předmět: | |
| DOI: | 10.18721/jpm.153.103 |
| Popis: | The modified Bridgeman method was used to obtain single crystals of (Cd0.69Zn0.31)3As2. It has been established that the studied sample crystallizes in space group P42/nmc with lattice parameters a = 8.78 Å, b = 12.42 Å. We have investigated the electrical conductivity in the temperature range from 10 to 300 K and in a magnetic field of 1 T, and determined the temperature dependences of the concentration and mobility of charge carriers. We have established that hopping conduction with a variable length of the Mott-type hop takes place in the temperature range from 10 to 33 K, and determined its micro parameters. Модифицированный метод Бриджмена был использован для получения монокристаллов (Cd0,69Zn0,31)3As2. Установлено, что исследуемый образец кристаллизуется в пространственной группе P42/nmc с параметрами решетки a = 8,78 Å, b = 12,42 Å. Была исследована электропроводность в диапазоне температур от 10 до 300 К и в магнитном поле 1 Тл, а также определены температурные зависимости концентрации и подвижности носителей заряда. Установлено, что в диапазоне температур от 10 до 33 К имеет место прыжковая проводимость с переменной длиной прыжка типа Мотта, и определены ее микропараметры. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|