| Popis: |
It is well known that piezoelectric ceramics are wildly used in many fields such as electrical sensors, actuators, alarm equipments etc. In this paper，the microstructure and the piezoelectric properties of Pb（Zr1/2Ti1/2）1-x（Nb2/3Mg1/3）xO3 (PMNZT) were studied. A novel B-site precursor method was adopted for preparing of Pb（Zr1/2Ti1/2）1-x（Nb2/3Mg1/3）xO3 samples. For investigating the crystallographic phase and microstructure of the samples, X-ray diffraction(XRD) and scanning electron microscopy(SEM) methods have been adopted respectively. The results show that a pure perovskite structure can be obtained after sintering at 1220°C for 2h. Through this experiment, it has been found that when sintering at 1220°C for 2h and the amounts of the Pbx（Nb2/3Mg1/3）xO3 (PMN) is 0.14, the Pb（Zr1/2Ti1/2）1-x（Nb2/3Mg1/3）xO3 samples are with the best electrical properties as follows: dielectric constant (ε) is 1858, dielectric loss(tanδ) is 0.017, electromechanical coupling coefficient (Kp) is 0.515, piezoelectric constant(d33) is 362PC/N |