An investigation of the use of strain gages to measure welding-induced residual stresses

Autor: D. S. Saunders, D. H. Sanford, M.Z.Shah Khan, N. J. Baldwin
Rok vydání: 1997
Předmět:
Zdroj: Experimental Mechanics. 37:264-271
ISSN: 1741-2765
0014-4851
DOI: 10.1007/bf02317417
Popis: The measurement of weld-induced residual stress is important in structures that are subjected to cyclic loading during their service life. Depending on their magnitude, stresses can influence the rate of crack growth under cyclic loading and hence affect the life of the structure. Because the level of residual stress may change during service, measurement of these changes is necessary for accurate life prediction of the structures. The measurement of welding-induced residual stress using strain gages poses significant problems, the most important being the potential damage to the gages by high temperatures generated in the welding process. This laboratory study was undertaken to assess the suitability and signal stability of commercially available resistive strain gages for the measurement of postweld residual stresses in a submarine hull structure. Adhesively bonded and weldable-type strain gages were attached to the surface of a 35 mm thick steel plate, which was then subjected to thermal cycles similar to those encountered during welding construction of a submarine pressure hull. This paper describes the strain gage application procedure, changes in the strain gage output at end of each experimental stage and the history of changes in the residual stress.
Databáze: OpenAIRE
Externí odkaz: