Grain-growth behavior and low-pressure oxygen compatibility of an Ir-0.3 wt.% W alloy
| Autor: | A.N. Gubbi, Easo P. George, Y. Lin, C.G. McKamey |
|---|---|
| Rok vydání: | 1996 |
| Předmět: |
Oxygen compatibility
Materials science Mechanical Engineering Metallurgy Alloy Metals and Alloys Oxide chemistry.chemical_element Partial pressure engineering.material Oxygen Grain size chemistry.chemical_compound Grain growth chemistry Mechanics of Materials Materials Chemistry engineering Grain boundary |
| Zdroj: | Journal of Alloys and Compounds. 244:175-183 |
| ISSN: | 0925-8388 |
| DOI: | 10.1016/s0925-8388(96)02425-5 |
| Popis: | The grain-growth behavior in a low-pressure oxygen-containing atmosphere of an Ir-0.3 wt.% W alloy (designated DOP-26) currently used for cladding of the 238-plutonium oxide fuel in radioisotope thermoelectric generators (RTGs) was studied. A small amount of added thorium improves the impact properties of this alloy partly by segregating to grain boundaries where it provides strengthening and partly by forming Ir 5 Th precipitates in the matrix which refine grain size. However, a previous preliminary study showed that, in an atmosphere containing a low partial pressure of oxygen (on the order of 1 mPa), the dissolution of the Ir 5 Th precipitates and diffusion of thorium to the surface to form ThO 2 was thermodynamically favorable, leading to anomalous growth of near-surface grains. In this study, specimens were exposed to an oxygen partial pressure of 1.3 mPa at temperatures of 1230, 1280 and 1330 °C for times up to 3000 h. The grain-growth behavior in a vacuum of 0.7 mPa was also determined as a comparison. The results substantiated the earlier study and showed that anomalous growth of near-surface grains does occur in this alloy. The results also indicated a marked difference in the kinetics of grain growth in the vacuum versus low-pressure oxygen atmospheres. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect