| Popis: |
The influence of Al content on microstructure and creep behavior of Ni3Al-Base single crystal superalloy was investigated. Two Ni3Al-Base single crystal alloys with different Al contents were prepared in a vacuum induction furnace by screw selection crystal method.Optical microscope (OM), differential scanning calorimetry (DSC),scanning electron microscope (SEM),energy dispersive spectrometer (EDS),and X-ray diffraction (XRD) were used to observe the microstructure of the alloys.The experimental results showed thatthe volume fraction, mean size of the eutectic phase γ-γ′, γ′before and after heat treatment display differences with the Al content. It has been found that the stress-rupture lives increased with theAl content.The reasons may be as follows.Firstly, as content of Al increases, the reinforcing phaseγ′increases, resulting in the improvement of the precipitation strengthening.And secondly, the increasing of Al content leadsthe decreasing lattice mismatch of γ/γ′ phase, which enhances the coherent strain field around theγ′ phase and the hence increase the strengthening effect to the alloy. |