PREVENTION OF WATER LEAKAGE IN CONCRETE BY CRACK-INDUCING JOINT APPLIED SUPERABSORBENT POLYMER

Autor: Yasuhiro Fuchita, Hiroyasu Kataoka, Takashi Hitomi
Rok vydání: 2012
Předmět:
Zdroj: Cement Science and Concrete Technology. 66:592-599
ISSN: 2187-3313
0916-3182
DOI: 10.14250/cement.66.592
Popis: For prevention of water leakage in concrete by crack-inducing joint applied polyvinyl chloride (PVC) pipe, waterproof rubber is applied to a PVC pipe. In this study, the authors developed and tested a new method that automatically stops water by coating superabsorbent polymer on the PVC pipe. Water penetration effect was tested for laboratory size and actual size specimens, and crack-inducing joint was applied to both the types of specimens. As a result, the specimen that coated superabsorbent polymer on the PVC pipe showed to induce water penetration, and confirmed the precipitation of cement-derived minerals such as calcium compounds at concrete around the PVC pipe. Furthermore, water penetration effect is expected for a long time.塩ビパイプを利用する誘発目地工法により発生したひび割れからの漏水を抑える機能を持たせるために、塩ビパイプに止水ゴムを取り付ける方法がある。本研究では、塩ビパイプにあらかじめ吸水ポリマーをコーティングすることにより、止水機能を自動的に発揮させる手法を新たに考案し、その効果を確認した。ひび割れ誘発目地を挿入した試験体による室内試験および実大寸法の壁試験体において、漏水防止効果の検証試験を行った。その結果、ノニオン型吸水ポリマーをコーティングした塩ビパイプで良好な漏水防止効果が得られた。更に、塩ビパイプ周りでカルシウム化合物等のセメント由来鉱物の析出が確認され、長期的な漏水防止効果が期待される。
Databáze: OpenAIRE
Externí odkaz: