Current Development Status and Future Challenges of Ferroelectric Random Access Memory Technologies
| Autor: | Kinam Kim, Sung-Yung Lee |
|---|---|
| Rok vydání: | 2006 |
| Předmět: |
Materials science
Physics and Astronomy (miscellaneous) business.industry Transistor General Engineering General Physics and Astronomy Ferroelectricity Ferroelectric capacitor law.invention Atomic layer deposition Hysteresis Capacitor law Etching Optoelectronics business Polarization (electrochemistry) |
| Zdroj: | Japanese Journal of Applied Physics. 45:3189-3193 |
| ISSN: | 1347-4065 0021-4922 |
| Popis: | For ferroelectric random access memory (FRAM) to be beneficial in future mobile devices, high-density FRAM with nm scaled cell should be developed. We have succeeded in scaling further the cell size of one-pass transistor and one-storage capacitor (1T1C) FRAM down to 0.27 µm2 at 150 nm technology node. Owing to new SrRuO3 (SRO) electrode technology along with ultrathin PbZrTiO3 (PZT) using metal organic chemical vapor deposition (MOCVD) technology, two-dimensional (2-D) metal–insulator–metal (MIM) ferroelectric capacitor was successfully scaled down vertically to 200 nm. By the application of a new double hard mask capacitor etching technology, 0.11-µm2-area 200-nm-thick 2-D PZT capacitor was successfully isolated with 180 nm spacing. As a result, a high remanent polarization of 40 µC/cm2 was obtained at 1.6 V on a 0.11 µm2 ferroelectric storage capacitor of the 0.27 µm2 cell 1T1C FRAM. Great advances in three-dimensional (3-D) ferroelectric capacitor, which is essential for 6–8 F2 cell 1T1C FRAM at nm scaled technology node, have been made by introducing a new atomic layer deposition (ALD) method for 3-D electrode and a novel MOCVD PZT deposition for 3-D PZT. As a result, for the first time, robust hysteresis was obtained from a 3-D PZT capacitor. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|