Investigations on the Characteristics of Thermally Sprayed NiCrBSi Coatings Fused by Flame and Inductive Processing
| Autor: | Y Kilic, Norbert Kazamer, Viorel-Aurel Șerban, D. T. Pascal, P C Valean, G. Marginean, Roxana Muntean |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Materials science
010308 nuclear & particles physics Alloy Hardfacing 02 engineering and technology engineering.material Microstructure 01 natural sciences Indentation hardness Corrosion 020303 mechanical engineering & transports 0203 mechanical engineering Coating 0103 physical sciences engineering Composite material Porosity Thermal spraying |
| Zdroj: | IOP Conference Series: Materials Science and Engineering. 416:012002 |
| ISSN: | 1757-899X |
| DOI: | 10.1088/1757-899x/416/1/012002 |
| Popis: | Ni-based materials are some of the most used hardfacing alloys to improve wear and corrosion resistance for parts functioning under severe conditions. For the current study, a NiCrBSi self-fluxing alloy powder with particle size in range of 45-106 μm was employed as feedstock material and deposited onto a steel substrate material using the oxyacetylene thermal spraying process. The as-sprayed components have been subsequently subjected to thermal post-processing in order to increase the adhesion to the substrate and to reduce the inherent porosity of the coatings. Consequently, two types of heating sources were chosen. One of them was the neutral oxyacetylene flame and the second one was based on high frequency currents. The aim of this work was to study the influence of the heat source type of the post treatment on the final characteristics of the coatings. Evaluation of the morphology and microstructure of the developed coatings was performed after the remelting process by means of scanning electron microscopy. Hardness tests were carried out in cross-section complying with the ASTM E384 standard. In both cases, after fusing, the microstructure was refined, with a drastic decrease in porosity. Evaluation of the hardness distribution along the coating cross-section revealed similar values of microhardness. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|