Ammonium salt-based steelmaking slag carbonation: Precipitation of CaCO3 and ammonia losses assessment
| Autor: | Arshe Said, Sanni Eloneva, Pekka Mannisto, Carl-Johan Fogelholm, Ron Zevenhoven |
|---|---|
| Rok vydání: | 2011 |
| Předmět: |
Environmental Engineering
Aqueous solution business.industry Precipitation (chemistry) Carbonation Inorganic chemistry Slag Steelmaking chemistry.chemical_compound Ammonia Calcium carbonate chemistry Chemical engineering visual_art visual_art.visual_art_medium Environmental Chemistry Ammonium business |
| Zdroj: | Greenhouse Gases: Science and Technology. 1:305-311 |
| ISSN: | 2152-3878 |
| DOI: | 10.1002/ghg.37 |
| Popis: | A mineral carbonation method based on steelmaking slags and ammonium salt solutions has been found to have economical and CO2 emission reduction potential. Although the aqueous solution of ammonium salt can be recycled, some of the solvent is likely to escape in a form of ammonia vapor within the outgoing gas flow during the carbonation step. In this study, the escape of ammonia vapor was investigated. The loss of NH3 was found to be quite insignificant and in addition, the total solution loss per step was very small. The CO2 content of the ingoing gas flow affected the rate of the CaCO3 precipitation; the smaller the CO2 content, the longer the duration of the carbonation reaction. However, the CO2 content did not seem to have a significant effect on the degree of CaCO3 precipitation, indicating that CO2 capture in a separate process step should not be needed. CaCO3 precipitated in a form of calcite, although two of the precipitates also contained aragonite. Furthermore, the precipitates were found to be of high quality with bright white color, and fine and powdery texture. Nonetheless, in order to obtain high-quality CaCO3, the precipitate resulting from the carbonation step should be washed with an adequate amount of water. © 2011 Society of Chemical Industry and John Wiley & Sons, Ltd |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Plný text